EAA PRIMACOR™ 5980I DOW USA
722
- Properties:High gloss
- Usages:Power tools
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 125℃/2.16kg | ASTM D-1238 | g/10min | |
| 190℃/2.16kg | ISO 1133 | 300 | g/10min | |
| Monomer content | % | Internal Method | 20.5 | |
| Melt mass flow rate | 190℃/2.16kg | ASTM D-1238 | 300 | g/10min |
| 125℃/2.16kg | ISO 1133 | g/10min | ||
| 125°C/2.16kg2 | ASTMD1238,ISO1133 | 14 | g/10min | |
| 190°C/2.16kg3 | ASTMD1238,ISO1133 | 300 | g/10min | |
| Content of comonomer | 内部方法 | 20.5 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore hardness | 邵氏D | ASTMD2240,ISO868 | 50 | |
| Tensile modulus -2% secant | 模压成型 | ASTMD638,ISO527-2 | 33.1 | Mpa |
| tensile strength | 断裂,模压成型 | ASTMD638,ISO527-2 | 9.65 | Mpa |
| elongation | 断裂,模压成型 | ASTMD638,ISO527-2 | 390 | % |
| Shore hardness | Shore D | ASTM D-2240 | ||
| Shore D | ISO 868 | |||
| Tensile modulus -2% Secant | Compression Molded | ASTM D-638 | Mpa | |
| Compression Molded | ISO 527-2 | Mpa | ||
| Tensile fracture strength | Compression Molded | ASTM D-638 | Mpa | |
| Compression Molded | ISO 527-2 | Mpa | ||
| Tensile strain at break | Compression Molded | ASTM D-638 | % | |
| Compression Molded | ISO 527-2 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | ASTM D-1525 | 42.2 | ℃ | |
| ISO 306 | 42.2 | ℃ | ||
| Melting temperature | ℃ | Internal Method | 77.2 | |
| vicat softening point | ASTMD1525,ISO306 | 42.2 | °C | |
| Melting temperature | 内部方法 | 77.2 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.