EAA PRIMACOR™ 5980I DOW USA
318
Unit Price:$9633 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High gloss
- Application Areas:Power tools
- Color:--
- Grade:Hot melt grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 125℃/2.16kg | ASTM D-1238 | g/10min | |
| 190℃/2.16kg | ISO 1133 | 300 | g/10min | |
| Monomer content | % | Internal Method | 20.5 | |
| Melt mass flow rate | 190℃/2.16kg | ASTM D-1238 | 300 | g/10min |
| 125℃/2.16kg | ISO 1133 | g/10min | ||
| 125°C/2.16kg2 | ASTMD1238,ISO1133 | 14 | g/10min | |
| 190°C/2.16kg3 | ASTMD1238,ISO1133 | 300 | g/10min | |
| Content of comonomer | 内部方法 | 20.5 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore hardness | Shore D | ASTMD2240,ISO868 | 50 | |
| Tensile modulus -2% secant | Compression Molded | ASTMD638,ISO527-2 | 33.1 | Mpa |
| tensile strength | Break,Compression Molded | ASTMD638,ISO527-2 | 9.65 | Mpa |
| elongation | Break,Compression Molded | ASTMD638,ISO527-2 | 390 | % |
| Shore hardness | Shore D | ASTM D-2240 | ||
| Shore D | ISO 868 | |||
| Tensile modulus -2% Secant | Compression Molded | ASTM D-638 | Mpa | |
| Compression Molded | ISO 527-2 | Mpa | ||
| Tensile fracture strength | Compression Molded | ASTM D-638 | Mpa | |
| Compression Molded | ISO 527-2 | Mpa | ||
| Tensile strain at break | Compression Molded | ASTM D-638 | % | |
| Compression Molded | ISO 527-2 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | ASTM D-1525 | 42.2 | ℃ | |
| ISO 306 | 42.2 | ℃ | ||
| Melting temperature | ℃ | Internal Method | 77.2 | |
| vicat softening point | ASTMD1525,ISO306 | 42.2 | °C | |
| Melting temperature | 内部方法 | 77.2 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.