Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
EAA 5980I DOW USA
PRIMACOR™
Power tools
High gloss
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
EAA/DOW USA/5980I
Monomer content
%
20.5
I
Content of comonomer
内部方法
%
2
Melt mass flow rate
125°C/2.16kg2
ASTMD1238,ISO1133
g/10min
1
Melt mass flow rate
190°C/2.16kg3
ASTMD1238,ISO1133
g/10min
3
Melt mass flow rate
125℃/2.16kg
ASTM D-1238
g/10min
Melt mass flow rate
190℃/2.16kg
ISO 1133
g/10min
3
Melt mass flow rate
190℃/2.16kg
ASTM D-1238
g/10min
3
Melt mass flow rate
125℃/2.16kg
ISO 1133
g/10min
Mechanical performance
Test Condition
Test Method
Unit
EAA/DOW USA/5980I
Tensile fracture strength
Compression Molded
ASTM D-638
Mpa
Tensile fracture strength
Compression Molded
ISO 527-2
Mpa
Tensile strain at break
Compression Molded
ASTM D-638
%
Tensile strain at break
Compression Molded
ISO 527-2
%
Tensile modulus -2% Secant
Compression Molded
ASTM D-638
Mpa
Tensile modulus -2% Secant
Compression Molded
ISO 527-2
Mpa
Tensile modulus -2% secant
模压成型
ASTMD638,ISO527-2
Mpa
3
tensile strength
断裂,模压成型
ASTMD638,ISO527-2
Mpa
9
elongation
断裂,模压成型
ASTMD638,ISO527-2
%
3
Thermal performance
Test Condition
Test Method
Unit
EAA/DOW USA/5980I
Melting temperature
内部方法
°C
7
Melting temperature
℃
77.2
I
vicat softening point
ASTMD1525,ISO306
°C
4
vicat softening point
ASTM D-1525
℃
4
vicat softening point
ISO 306
℃
4