MMW-HDPE TOTAL Polyethylene HDPE HL 535 TOTAL
0
- 典型应用:Filmbaglining
比对物性数据
| 物理性能 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 密度 | ASTMD792 | 0.955 g/cm³ | |
| 熔体质量流动速率 | 190°C/2.16kg | ASTMD1238 | 0.35 g/10min |
| 190°C/21.6kg | ASTMD1238 | 30 g/10min |
| 薄膜 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 薄膜厚度-经测试 | 25 µm | ||
| 割线模量 | 25µm,BlownFilm | ASTMD882A | 917 MPa |
| 25µm,BlownFilm | ASTMD882A | 1280 MPa | |
| 拉伸强度 | Yield,25µm,BlownFilm | ASTMD882A | 27.6 MPa |
| Yield,25µm,BlownFilm | ASTMD882A | 29.6 MPa | |
| 拉伸应变-MD | Break,25µm,BlownFilm | ASTMD882A | 500 % |
| 拉伸应变 | Break,25µm,BlownFilm | ASTMD882A | 25 % |
| 落锤冲击 | 25µm,吹塑薄膜 | ASTMD1709A | <50 g |
| ElmendorfTearStrength-MD | 25µm,BlownFilm | ASTMD1922 | 8.0 g |
| ElmendorfTearStrength-TD | 25µm,BlownFilm | ASTMD1922 | 1100 g |
| WaterVaporTransmissionRate | 38°C,25µm,BlownFilm | ASTMF1249 | 11 g/m²/24hr |
| 拉伸强度 | Break,25µm,BlownFilm | ASTMD882A | 43.4 MPa |
| Break,25µm,BlownFilm | ASTMD882A | 29.6 MPa |
| 热性能 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 熔融峰值温度 | ASTMD3417 | 132 °C |
免责声明：此数据表中的信息由 Plas.Com 从该材料的生产商或第三方处获得。Plas.Com 尽最大努力确保此数据的准确性。 但是 Plas.Com 对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。