LDPE Petrothene® NA373244
0
- 典型应用:薄膜流延薄膜
比对物性数据
| 物理性能 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 密度 | ASTM D1505 | 0.924 g/cm³ | |
| 熔体质量流动速率 | 190°C/2.16kg | ASTM D1238 | 3.0 g/10min |
| 光学性能 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 光泽度 | 45°,31.8µm,BlownFilm | ASTM D2457 | 70 |
| 45°,31.8µm,CastFilm | ASTM D2457 | 77 | |
| 雾度 | 31.8µm,BlownFilm | ASTM D1003 | 5.4 % |
| 31.8µm,铸造薄膜 | ASTM D1003 | 3.4 % |
| 薄膜 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 埃尔曼多夫撕裂强度 | 32µm,BlownFilm，TD | ASTM D1922 | 170 g |
| 32µm,CastFilm，TD | ASTM D1922 | 160 g | |
| 拉伸强度 | Break,32µm,BlownFilm | ASTM D882 | 18.6 MPa |
| Break,32µm,CastFilm | ASTM D882 | 29.1 MPa | |
| Break,32µm,BlownFilm | ASTM D882 | 17.2 MPa | |
| Break,32µm,CastFilm | ASTM D882 | 17.0 MPa | |
| 伸长率 | Break,32µm,BlownFilm | ASTM D882 | 200 % |
| Break,32µm,CastFilm | ASTM D882 | 230 % | |
| 拉伸应变 | Break,32µm,BlownFilm | ASTM D882 | 500 % |
| 薄膜厚度 | 32 µm | ||
| 割线模量 | 32µm,BlownFilm | ASTM D882 | 159 MPa |
| 32µm,CastFilm | ASTM D882 | 208 MPa | |
| 落镖冲击 | 32µm,CastFilm | ASTM D1709 | 110 g |
| 埃尔曼多夫撕裂强度 | 32µm,BlownFilm，MD | ASTM D1922 | 270 g |
| 32µm,CastFilm，MD | ASTM D1922 | 300 g | |
| 割线模量 | 32µm,BlownFilm | ASTM D882 | 172 MPa |
| 32µm,CastFilm | ASTM D882 | 197 MPa | |
| 拉伸强度 | Yield,32µm,BlownFilm | ASTM D882 | 10.9 MPa |
| Yield,32µm,CastFilm | ASTM D882 | 9.38 MPa | |
| Yield,32µm,BlownFilm | ASTM D882 | 10.7 MPa | |
| Yield,32µm,CastFilm | ASTM D882 | 9.31 MPa | |
| 拉伸应变 | Break,32µm,CastFilm | ASTM D882 | 610 % |
| 落镖冲击 | 32µm,BlownFilm | ASTM D1709 | 65 g |
免责声明：此数据表中的信息由 Plas.Com 从该材料的生产商或第三方处获得。Plas.Com 尽最大努力确保此数据的准确性。 但是 Plas.Com 对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。