LDPE Petrothene® NA373244 HMC Polymers
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | HMC Polymers/Petrothene® NA373244 |
|---|---|---|---|
| Elmendorf tear strength | 32µm,CastFilm，TD | ASTM D1922 | 160 g |
| 32µm,BlownFilm，TD | ASTM D1922 | 170 g | |
| Secant modulus | 32µm,BlownFilm | ASTM D882 | 172 MPa |
| Dart impact | 32µm,CastFilm | ASTM D1709 | 110 g |
| tensile strength | Break,32µm,CastFilm | ASTM D882 | 17.0 MPa |
| Tensile strain | Break,32µm,BlownFilm | ASTM D882 | 500 % |
| tensile strength | Yield,32µm,CastFilm | ASTM D882 | 9.31 MPa |
| Dart impact | 32µm,BlownFilm | ASTM D1709 | 65 g |
| Elmendorf tear strength | 32µm,BlownFilm，MD | ASTM D1922 | 270 g |
| Tensile strain | Break,32µm,CastFilm | ASTM D882 | 610 % |
| elongation | Break,32µm,BlownFilm | ASTM D882 | 200 % |
| Secant modulus | 32µm,CastFilm | ASTM D882 | 197 MPa |
| tensile strength | Yield,32µm,BlownFilm | ASTM D882 | 10.7 MPa |
| film thickness | 32 µm | ||
| tensile strength | Break,32µm,BlownFilm | ASTM D882 | 17.2 MPa |
| elongation | Break,32µm,CastFilm | ASTM D882 | 230 % |
| Elmendorf tear strength | 32µm,CastFilm，MD | ASTM D1922 | 300 g |
| optical performance | Test Condition | Test Method | HMC Polymers/Petrothene® NA373244 |
|---|---|---|---|
| gloss | 45°,31.8µm,CastFilm | ASTM D2457 | 77 |
| Haze ratio | 31.8µm,BlownFilm | ASTM D1003 | 5.4 % |
| gloss | 45°,31.8µm,BlownFilm | ASTM D2457 | 70 |
| Haze ratio | 31.8µm,铸造薄膜 | ASTM D1003 | 3.4 % |
| physical property | Test Condition | Test Method | HMC Polymers/Petrothene® NA373244 |
|---|---|---|---|
| density | ASTM D1505 | 0.924 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 3.0 g/10min |