SBC Generic SBC Generic
0
- 特性:物理性能
比对物性数据
| 测试条件 | 测试方法 | 测试结果 | |
|---|---|---|---|
| 密度 | -- | ASTM D792 | 0.898to1.07 g/cm³ |
| 23°C | ISO 1183 | 0.886to1.09 g/cm³ | |
| 熔体质量流动速率 | 200°C/5.0kg | ASTM D1238 | 1.0to15 g/10min |
| 200°C/5.0kg | ISO 1133 | 3.4to8.0 g/10min | |
| 熔体体积流动速率 | 200°C/5.0kg | ISO 1133 | 10.9to12.1 cm³/10min |
| 收缩率 | MD:23°C | ASTM D955 | 0.60to0.68 % |
| 23°C | ISO 294-4 | 0.50to2.4 % | |
| 邵氏硬度 | 23°C | ASTM D2240 | 47to92 |
| 23°C | ISO 868 | 39to91 | |
| 弯曲模量 | 23°C | ASTM D790 | 1330to1800 MPa |
| 23°C | ISO 178 | 1380to2460 MPa | |
| 弯曲强度 | 23°C | ISO 178 | 16.5to76.5 MPa |
| 屈服,23°C | ASTM D790 | 24.4to54.0 MPa | |
| 拉伸强度 | 100%应变,23°C | ISO 37 | 1.80to5.38 MPa |
| 屈服,23°C | ASTM D638 | 1.03to33.4 MPa | |
| 200%应变,23°C | ISO 37 | 1.70to6.90 MPa | |
| 300%应变,23°C | ASTM D412 | 2.00to4.57 MPa | |
| 300%应变,23°C | ISO 37 | 1.00to8.00 MPa | |
| 屈服,23°C | ISO 37 | 1.70to33.0 MPa | |
| 雾度 | ASTM D1003 | 0.20to3.1 % | |
| 拉伸强度 | 屈服,23°C | ISO 527-2 | 4.00to51.0 MPa |
| 断裂,23°C | ISO 527-2 | 14.0to64.0 MPa | |
| 拉伸应变 | 屈服,23°C | ISO 527-2 | 2.0to2.1 % |
| 断裂,23°C | ASTM D638 | 30to260 % | |
| 标称拉伸断裂应变 | 23°C | ISO 527-2 | 2.5to500 % |
| 拉伸强度 | 断裂,23°C | ASTM D412 | 3.96to20.3 MPa |
| 伸长率 | 断裂,23°C | ASTM D412 | 550to850 % |
| 断裂,23°C | ISO 37 | 400to890 % | |
| 撕裂强度 | 23°C | ASTM D624 | 19.8to104 kN/m |
| 23°C | ISO 34-1 | 18to110 kN/m | |
| 压缩永久变形 | 23°C | ISO 815 | 18to36 % |
| 简支梁缺口冲击强度 | 23°C | ISO 179 | 1.6to9.9 kJ/m² |
| 悬壁梁缺口冲击强度 | 23°C | ASTM D256 | 20to110 J/m |
| 落镖冲击 | 23°C | ASTM D3763 | 0.602to41.6 J |
| 最高连续使用温度 | SAEJ2236 | 150to170 °C | |
| 热变形温度 | 1.8MPa,未退火，HDT | ASTM D648 | 59.6to62.7 °C |
| 脆化温度 | ASTM D746 | -60.0--59.0 °C | |
| 维卡软化温度 | -- | ASTM D1525 | 62.7to90.0 °C |
| -- | ISO 306 | 62.0to93.5 °C | |
| 燃烧速率 | ISO 3795 | 37to54 mm/min | |
| 透射率 | ASTM D1003 | 88.9to93.1 % |
免责声明：此数据表中的信息由 Plas.Com 从该材料的生产商或第三方处获得。Plas.Com 尽最大努力确保此数据的准确性。 但是 Plas.Com 对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。