SBC Generic SBC Generic
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Test Condition | Test Method | Generic/Generic SBC | |
|---|---|---|---|
| tensile strength | 100%应变,23°C | ISO 37 | 1.80to5.38 MPa |
| Flexural modulus | 23°C | ISO 178 | 1380to2460 MPa |
| tensile strength | 300%应变,23°C | ASTM D412 | 2.00to4.57 MPa |
| density | -- | ASTM D792 | 0.898to1.07 g/cm³ |
| tensile strength | 300%应变,23°C | ISO 37 | 1.00to8.00 MPa |
| 屈服,23°C | ISO 37 | 1.70to33.0 MPa | |
| Nominal tensile fracture strain | 23°C | ISO 527-2 | 2.5to500 % |
| elongation | 断裂,23°C | ISO 37 | 400to890 % |
| transmissivity | ASTM D1003 | 88.9to93.1 % | |
| tensile strength | 屈服,23°C | ISO 527-2 | 4.00to51.0 MPa |
| Tensile strain | 断裂,23°C | ASTM D638 | 30to260 % |
| tear strength | 23°C | ASTM D624 | 19.8to104 kN/m |
| Flexural modulus | 23°C | ASTM D790 | 1330to1800 MPa |
| tensile strength | 断裂,23°C | ISO 527-2 | 14.0to64.0 MPa |
| 屈服,23°C | ASTM D638 | 1.03to33.4 MPa | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 59.6to62.7 °C |
| tensile strength | 断裂,23°C | ASTM D412 | 3.96to20.3 MPa |
| bending strength | 屈服,23°C | ASTM D790 | 24.4to54.0 MPa |
| vicat | -- | ASTM D1525 | 62.7to90.0 °C |
| tear strength | 23°C | ISO 34-1 | 18to110 kN/m |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 20to110 J/m |
| Maximum continuous use temperature | SAEJ2236 | 150to170 °C | |
| melt mass-flow rate | 200°C/5.0kg | ISO 1133 | 3.4to8.0 g/10min |
| bending strength | 23°C | ISO 178 | 16.5to76.5 MPa |
| tensile strength | 200%应变,23°C | ISO 37 | 1.70to6.90 MPa |
| Charpy Notched Impact Strength | 23°C | ISO 179 | 1.6to9.9 kJ/m² |
| brittle temperature | ASTM D746 | -60.0--59.0 °C | |
| burning rate | ISO 3795 | 37to54 mm/min | |
| compression set | 23°C | ISO 815 | 18to36 % |
| Shrinkage rate | MD:23°C | ASTM D955 | 0.60to0.68 % |
| Shore hardness | 23°C | ISO 868 | 39to91 |
| Haze ratio | ASTM D1003 | 0.20to3.1 % | |
| vicat | -- | ISO 306 | 62.0to93.5 °C |
| density | 23°C | ISO 1183 | 0.886to1.09 g/cm³ |
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 1.0to15 g/10min |
| Tensile strain | 屈服,23°C | ISO 527-2 | 2.0to2.1 % |
| Dart impact | 23°C | ASTM D3763 | 0.602to41.6 J |
| Shore hardness | 23°C | ASTM D2240 | 47to92 |
| elongation | 断裂,23°C | ASTM D412 | 550to850 % |
| Melt volume flow rate | 200°C/5.0kg | ISO 1133 | 10.9to12.1 cm³/10min |
| Shrinkage rate | 23°C | ISO 294-4 | 0.50to2.4 % |