物性数据
| 物理性能 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 收缩率 | MD：1.59mm | ASTM D955 | 1.4 % |
| 收缩率 | MD：3.18mm | ASTM D955 | 1.3 % |
| 收缩率 | TD：1.59mm | ASTM D955 | 0.50 % |
| 收缩率 | TD：3.18mm | ASTM D955 | 1.1 % |
| 收缩率 | TD:1.59mm | ISO 294-4 | 0.50 % |
| 收缩率 | MD:1.59mm | ISO 294-4 | 1.4 % |
| 收缩率 | TD:3.18mm | ISO 294-4 | 1.1 % |
| 收缩率 | MD:3.18mm | ISO 294-4 | 1.3 % |
| MeltViscosity | 190°C,300sec^-1 | ASTM D3835 | 219 Pa·s |
| 弹性体 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 拉伸永久变形 | 100%应变 | ASTM D412 | 16 % |
| 拉伸强度 | 100%应变 | ASTM D412 | 2.54 Mpa |
| 拉伸强度 | 100%应变,23°C | ISO 37 | 2.54 Mpa |
| 拉伸强度 | 屈服,23°C | ASTM D412 | 8.30 Mpa |
| 拉伸强度 | 屈服,23°C | ISO 37 | 8.30 Mpa |
| 伸长率 | 断裂 | ASTM D412 | 310 % |
| 伸长率 | 断裂,23°C | ISO 37 | 310 % |
| 撕裂强度 | 24°C | ASTM D624 | 33.4 kN/m |
| 压缩永久变形 | 24°C,22hr | ASTM D395B | 26 % |
| 压缩永久变形 | 70°C,22hr | ASTM D395B | 48 % |
| 压缩永久变形 | 100°C,22hr | ASTM D395B | 63 % |
| 压缩永久变形 | 24°C,22hr | ISO 815 | 26 % |
| 压缩永久变形 | 70°C,22hr | ISO 815 | 48 % |
| 压缩永久变形 | 100°C,22hr | ISO 815 | 63 % |
| 硬度 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 邵氏硬度 | 邵氏A,5秒 | ASTM D2240 | 78 |
| 邵氏硬度 | 邵氏A,5秒 | ISO 868 | 78 |
| 热性能 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 脆化温度 | | ASTM D746 | -61.1 °C |
| 脆化温度 | | ISO 812 | -61.1 °C |
| 老化 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 拉伸应力变化率 | 70°C,168hr，断裂 | ISO 1817 | -5.0 % |
| 拉伸应力变化率 | 100°C,168hr，断裂 | ISO 1817 | 4.0 % |
| 体积变化 | 24°C,168hr,inReferenceFuelB | ASTM D471 | 54 % |
| 体积变化 | 100°C,168hr,inASTM#1Oil | ASTM D471 | 6.0 % |
| 体积变化 | 100°C,168hr,inIRM903Oil | ASTM D471 | 82 % |
| 体积变化 | 100°C,168hr,在水中 | ASTM D471 | 1.0 % |
| 体积变化 | 24°C,168hr,inReferenceFuelB | ISO 1817 | 54 % |
| 体积变化 | 100°C,168hr,inASTM#1Oil | ISO 1817 | 6.0 % |
| 体积变化 | 100°C,168hr,inIRM903Oil | ISO 1817 | 82 % |
| 体积变化 | 100°C,168hr,在水中 | ISO 1817 | 1.0 % |
| 空气中拉伸强度的变化率 | 70°C,168hr | ASTM D573 | -2.0 % |
| 空气中拉伸强度的变化率 | 100%Strain,70°C,168hr | ASTM D573 | 7.0 % |
| 空气中拉伸强度的变化率 | 100°C,168hr | ASTM D573 | -2.0 % |
| 空气中拉伸强度的变化率 | 100%Strain,100°C,168hr | ASTM D573 | 7.0 % |
| 空气中拉伸强度的变化率 | 70°C,168hr | ISO 188 | -2.0 % |
| 空气中拉伸强度的变化率 | 100%Strain70°C,168hr | ISO 188 | 7.0 % |
| 空气中拉伸强度的变化率 | 100°C,168hr | ISO 188 | -2.0 % |
| 空气中拉伸强度的变化率 | 100%Strain100°C,168hr | ISO 188 | 7.0 % |
| 空气中极限伸长率的变化率 | 70°C,168hr | ASTM D573 | -5.0 % |
| 空气中极限伸长率的变化率 | 100°C,168hr | ASTM D573 | 4.0 % |
| 机械性能 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 泰伯（Taber）耐磨性 | 1000Cycles,1.0E+6g,CS-17Wheel | ASTM D1044 | 12.5 mg |
免责声明：此数据表中的信息由 Plas.Com 从该材料的生产商或第三方处获得。Plas.Com 尽最大努力确保此数据的准确性。 但是 Plas.Com 对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。