Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TPE DGR6080 APA USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | APA USA/DGR6080 |
|---|---|---|---|
| Shore hardness | 邵氏A,5秒 | ISO 868 | 78 |
| 邵氏A,5秒 | ASTM D2240 | 78 |
| Mechanical properties | Test Condition | Test Method | APA USA/DGR6080 |
|---|---|---|---|
| Taber wear resistance | 1000Cycles,1.0E+6g,CS-17Wheel | ASTM D1044 | 12.5 mg |
| elastomer | Test Condition | Test Method | APA USA/DGR6080 |
|---|---|---|---|
| tensile strength | 100%应变 | ASTM D412 | 2.54 Mpa |
| elongation | 断裂 | ASTM D412 | 310 % |
| compression set | 70°C,22hr | ASTM D395B | 48 % |
| tensile strength | 屈服,23°C | ISO 37 | 8.30 Mpa |
| 100%应变,23°C | ISO 37 | 2.54 Mpa | |
| tear strength | 24°C | ASTM D624 | 33.4 kN/m |
| Stretch permanent deformation | 100%应变 | ASTM D412 | 16 % |
| compression set | 100°C,22hr | ISO 815 | 63 % |
| 100°C,22hr | ASTM D395B | 63 % | |
| elongation | 断裂,23°C | ISO 37 | 310 % |
| compression set | 70°C,22hr | ISO 815 | 48 % |
| tensile strength | 屈服,23°C | ASTM D412 | 8.30 Mpa |
| compression set | 24°C,22hr | ISO 815 | 26 % |
| 24°C,22hr | ASTM D395B | 26 % |
| aging | Test Condition | Test Method | APA USA/DGR6080 |
|---|---|---|---|
| Change rate of tensile strength in air | 70°C,168hr | ASTM D573 | -2.0 % |
| 100%Strain,100°C,168hr | ASTM D573 | 7.0 % | |
| volume change | 100°C,168hr,inIRM903Oil | ASTM D471 | 82 % |
| Change rate of tensile strength in air | 100°C,168hr | ASTM D573 | -2.0 % |
| volume change | 24°C,168hr,inReferenceFuelB | ASTM D471 | 54 % |
| Change rate of tensile strength in air | 100%Strain100°C,168hr | ISO 188 | 7.0 % |
| 100%Strain,70°C,168hr | ASTM D573 | 7.0 % | |
| volume change | 24°C,168hr,inReferenceFuelB | ISO 1817 | 54 % |
| 100°C,168hr,在水中 | ASTM D471 | 1.0 % | |
| 100°C,168hr,inIRM903Oil | ISO 1817 | 82 % | |
| Change rate of tensile strength in air | 100%Strain70°C,168hr | ISO 188 | 7.0 % |
| Change rate of ultimate elongation in air | 100°C,168hr | ASTM D573 | 4.0 % |
| Change rate of tensile strength in air | 70°C,168hr | ISO 188 | -2.0 % |
| 100°C,168hr | ISO 188 | -2.0 % | |
| Tensile stress change rate | 70°C,168hr，断裂 | ISO 1817 | -5.0 % |
| volume change | 100°C,168hr,inASTM#1Oil | ASTM D471 | 6.0 % |
| Tensile stress change rate | 100°C,168hr，断裂 | ISO 1817 | 4.0 % |
| volume change | 100°C,168hr,inASTM#1Oil | ISO 1817 | 6.0 % |
| 100°C,168hr,在水中 | ISO 1817 | 1.0 % | |
| Change rate of ultimate elongation in air | 70°C,168hr | ASTM D573 | -5.0 % |
| physical property | Test Condition | Test Method | APA USA/DGR6080 |
|---|---|---|---|
| Shrinkage rate | TD：3.18mm | ASTM D955 | 1.1 % |
| TD:1.59mm | ISO 294-4 | 0.50 % | |
| MD：1.59mm | ASTM D955 | 1.4 % | |
| MeltViscosity | 190°C,300sec^-1 | ASTM D3835 | 219 Pa·s |
| Shrinkage rate | MD:3.18mm | ISO 294-4 | 1.3 % |
| TD：1.59mm | ASTM D955 | 0.50 % | |
| MD：3.18mm | ASTM D955 | 1.3 % | |
| TD:3.18mm | ISO 294-4 | 1.1 % | |
| MD:1.59mm | ISO 294-4 | 1.4 % |
| Thermal performance | Test Condition | Test Method | APA USA/DGR6080 |
|---|---|---|---|
| brittle temperature | ISO 812 | -61.1 °C | |
| ASTM D746 | -61.1 °C |