TPU-Capro IROGRAN® A 95 K 4640 美国亨斯迈
0
比对物性数据
| 物理性能 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 熔体体积流动速率 | 210°C/2.16kg | 5.00to10.0 cm³/10min | |
| 收缩率 | MD：注塑 | ASTM D972 | 0.80 % |
| 密度 | ASTM D792 | 1.19 g/cm³ | |
| DIN 53479 | 1.19 g/cm³ |
| 弹性体 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 压缩永久变形 | 100°C,24hr | DIN 53517 | 25 % |
| 100°C,70hr | DIN 53517 | 38 % | |
| 23°C,24hr | ASTM D395 | 14 % | |
| 70°C,24hr | ASTM D395 | 25 % | |
| 100°C,24hr | ASTM D395 | 33 % | |
| 100°C,70hr | ASTM D395 | 38 % | |
| 23°C,24hr | DIN 53517 | 14 % | |
| 70°C,24hr | DIN 53517 | 23 % | |
| 撕裂强度 | DIN 53515 | 90 kN/m | |
| 拉伸强度 | 50%应变 | ASTM D412 | 8.62 MPa |
| 50%应变 | DIN 53504 | 9.00 MPa | |
| 100%应变 | ASTM D412 | 10.8 MPa | |
| 100%应变 | DIN 53504 | 11.5 MPa | |
| 200%Strain | ASTM D412 | 14.0 MPa | |
| 200%Strain | DIN 53504 | 14.2 MPa | |
| 300%应变 | ASTM D412 | 18.9 MPa | |
| 300%应变 | DIN 53504 | 20.4 MPa | |
| 断裂 | ASTM D412 | 37.2 MPa | |
| 断裂 | DIN 53504 | 53.0 MPa | |
| 伸长率 | 断裂 | ASTM D412 | 570 % |
| 断裂 | DIN 53504 | 530 % | |
| 撕裂强度 | ASTM D624 | 126 kN/m |
| 硬度 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 邵氏硬度 | 邵氏A,注塑 | ASTM D2240 | 95 |
| 邵氏D,注塑 | DIN 53505 | 45 | |
| 邵氏D,注塑 | ASTM D2240 | 45 | |
| 邵氏A,注塑 | DIN 53505 | 95 |
| 热性能 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 维卡软化温度 | DIN 53372 | 165 °C |
| 机械性能 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 拉伸强度 | ASTM D412 | 6.69 MPa | |
| 20%Strain | DIN 53504 | 7.00 MPa | |
| 耐磨性 | -- | ASTM D395 | 29 mm³ |
| -- | DIN 53516 | 30 mm³ |
免责声明：此数据表中的信息由 Plas.Com 从该材料的生产商或第三方处获得。Plas.Com 尽最大努力确保此数据的准确性。 但是 Plas.Com 对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。