Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TPU-Capro IROGRAN® A 95 K 4640 HUNTSMAN USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | HUNTSMAN USA/IROGRAN® A 95 K 4640 |
|---|---|---|---|
| Shore hardness | 邵氏A,注塑 | DIN 53505 | 95 |
| 邵氏A,注塑 | ASTM D2240 | 95 | |
| 邵氏D,注塑 | ASTM D2240 | 45 | |
| 邵氏D,注塑 | DIN 53505 | 45 |
| Mechanical properties | Test Condition | Test Method | HUNTSMAN USA/IROGRAN® A 95 K 4640 |
|---|---|---|---|
| tensile strength | 20%Strain | DIN 53504 | 7.00 MPa |
| ASTM D412 | 6.69 MPa | ||
| wear resistance | -- | DIN 53516 | 30 mm³ |
| -- | ASTM D395 | 29 mm³ |
| elastomer | Test Condition | Test Method | HUNTSMAN USA/IROGRAN® A 95 K 4640 |
|---|---|---|---|
| elongation | 断裂 | ASTM D412 | 570 % |
| compression set | 100°C,24hr | ASTM D395 | 33 % |
| 70°C,24hr | ASTM D395 | 25 % | |
| tensile strength | 50%应变 | DIN 53504 | 9.00 MPa |
| compression set | 23°C,24hr | ASTM D395 | 14 % |
| 100°C,70hr | ASTM D395 | 38 % | |
| tear strength | DIN 53515 | 90 kN/m | |
| compression set | 23°C,24hr | DIN 53517 | 14 % |
| tensile strength | 断裂 | DIN 53504 | 53.0 MPa |
| 300%应变 | ASTM D412 | 18.9 MPa | |
| compression set | 100°C,24hr | DIN 53517 | 25 % |
| 70°C,24hr | DIN 53517 | 23 % | |
| 100°C,70hr | DIN 53517 | 38 % | |
| tensile strength | 断裂 | ASTM D412 | 37.2 MPa |
| 100%应变 | DIN 53504 | 11.5 MPa | |
| 50%应变 | ASTM D412 | 8.62 MPa | |
| 300%应变 | DIN 53504 | 20.4 MPa | |
| 100%应变 | ASTM D412 | 10.8 MPa | |
| 200%Strain | ASTM D412 | 14.0 MPa | |
| elongation | 断裂 | DIN 53504 | 530 % |
| tensile strength | 200%Strain | DIN 53504 | 14.2 MPa |
| tear strength | ASTM D624 | 126 kN/m |
| physical property | Test Condition | Test Method | HUNTSMAN USA/IROGRAN® A 95 K 4640 |
|---|---|---|---|
| density | DIN 53479 | 1.19 g/cm³ | |
| Melt volume flow rate | 210°C/2.16kg | 5.00to10.0 cm³/10min | |
| density | ASTM D792 | 1.19 g/cm³ | |
| Shrinkage rate | MD：注塑 | ASTM D972 | 0.80 % |
| Thermal performance | Test Condition | Test Method | HUNTSMAN USA/IROGRAN® A 95 K 4640 |
|---|---|---|---|
| vicat | DIN 53372 | 165 °C |