TPV Santoprene™ 8211-55B100 美国塞拉尼斯
30
- 特性:耐磨耐老化抗紫外线耐候高流动可回收材料良好粘结性表面光洁度佳良好成型性能良好的柔韧性良好的着色性耐臭氧性能外观良好
- 典型应用:厨具家用电器电器用具家电部件活动的铰链镜架密封件疲劳消除用品汽车领域发动机罩零件柔软的把手智能手机体育用品消费品领域粘合粘结树脂
比对
查看报价物性数据
| 弹性体 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 伸长率-横向流量 | 断裂,23°C | ASTMD412 | 600 % |
| 断裂,23°C | ISO37 | 600 % | |
| CompressionSet2 | 125°C,70hr | ASTMD395B | 55 % |
| CompressionSet3 | 125°C,70hr | ISO815 | 55 % |
| 硬度 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 肖氏硬度 | 邵氏A,15秒,23°C | ISO868 | 53 |
| 老化 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 空气中拉伸强度的变化率 | 100°C,168hr | ASTMD573 | -28 % |
| 125°C,168hr | ASTMD573 | -61 % | |
| 100°C,168hr | ISO188 | -28 % | |
| 125°C,168hr | ISO188 | -61 % | |
| 硬度计硬度的变化率2 | ShoreA,23°C,168hr,inIRM903Oil | ASTMD471 | -33 |
| ShoreA,23°C,168hr,inSodiumHydroxide,50% | ASTMD471 | 4.0 | |
| ShoreA,23°C,168hr,inWater | ASTMD471 | 5.0 | |
| ChangeinShoreHardness | ShoreA,23°C,168hr,inEthanol,95% | ISO1817 | 2.0 |
| ShoreA,23°C,168hr,inHydrochloricAcid,10% | ISO1817 | 4.0 | |
| ShoreA,23°C,168hr,inIRM903Oil | ISO1817 | -33 | |
| ShoreA,23°C,168hr,inSodiumHydroxide,50% | ISO1817 | 4.0 | |
| ShoreA,23°C,168hr,inWater | ISO1817 | 5.0 | |
| 空气中极限伸长率的变化率 | 100°C,168hr | ASTMD573 | -14 % |
| 125°C,168hr | ASTMD573 | -70 % | |
| 在空气中断裂时拉伸应力变化 | 100°C,168hr | ISO188 | -14 % |
| 125°C,168hr | ISO188 | -70 % | |
| 空气中硬度计硬度的变化率 | ShoreA,100°C,168hr | ASTMD573 | -4.0 |
| 邵氏A,125°C,168hr | ASTMD573 | 8.0 | |
| 空气中邵氏硬度的变化率 | ShoreA,100°C,168hr | ISO188 | -4.0 |
| 邵氏A,125°C,168hr | ISO188 | 8.0 | |
| 拉伸强度的变化率 | 23°C,168hr,inEthanol,95% | ASTMD471 | -17 % |
| 23°C,168hr,inHydrochloricAcid,10% | ASTMD471 | -1.0 % | |
| 极限伸长率的变化率 | 23°C,168hr,inIRM903Oil | ASTMD471 | -68 % |
| 23°C,168hr,inSodiumHydroxide,50% | ASTMD471 | -7.0 % | |
| 23°C,168hr,在水中 | ASTMD471 | -12 % | |
| 断裂时拉伸应力变化 | 23°C,168hr,inEthanol,95% | ISO1817 | -3.0 % |
| 23°C,168hr,inHydrochloricAcid,10% | ISO1817 | -9.0 % | |
| 23°C,168hr,inIRM903Oil | ISO1817 | -68 % | |
| 23°C,168hr,inSodiumHydroxide,50% | ISO1817 | -7.0 % | |
| 23°C,168hr,在水中 | ISO1817 | -12 % | |
| 硬度计硬度的变化率2 | ShoreA,23°C,168hr,inEthanol,95% | ASTMD471 | 2.0 |
| ShoreA,23°C,168hr,inHydrochloricAcid,10% | ASTMD471 | 4.0 | |
| 拉伸强度的变化率 | 23°C,168hr,inIRM903Oil | ASTMD471 | -85 % |
| 23°C,168hr,inSodiumHydroxide,50% | ASTMD471 | 1.0 % | |
| 23°C,168hr,在水中 | ASTMD471 | 2.0 % | |
| 23°C,168hr,inEthanol,95% | ISO1817 | -17 % | |
| 23°C,168hr,inHydrochloricAcid,10% | ISO1817 | -1.0 % | |
| 23°C,168hr,inIRM903Oil | ISO1817 | -85 % | |
| 23°C,168hr,inSodiumHydroxide,50% | ISO1817 | 1.0 % | |
| 23°C,168hr,在水中 | ISO1817 | 2.0 % | |
| 极限伸长率的变化率 | 23°C,168hr,inEthanol,95% | ASTMD471 | -3.0 % |
| 23°C,168hr,inHydrochloricAcid,10% | ASTMD471 | -9.0 % |
| 可燃性 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| UL阻燃等级 | 1.1mm | UL94 | HB |
| 2.9mm | UL94 | HB |
免责声明：此数据表中的信息由 Plas.Com 从该材料的生产商或第三方处获得。Plas.Com 尽最大努力确保此数据的准确性。 但是 Plas.Com 对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。