Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TPV 8211-55B100 CELANESE USA
Santoprene™
Kitchen utensils,Household appliances,Electrical appliances,Home appliance components,Movable hinge,Mirror frame,packing,Fatigue relief supplies,Automotive sector,Engine hood parts,Soft handle,Smart phone,sporting goods,Consumer goods sector,Bonding,Adhesive resin
wear resistant,Aging resistance,UV resistance,Weather resistance,High mobility,Recyclable materials,Good adhesion,Excellent surface finish,Good forming performance,Good flexibility,Good colorability,Ozone resistance,Good appearance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | CELANESE USA/8211-55B100 |
|---|---|---|---|
| Shore hardness | 邵氏A,15秒,23°C | ISO 868 | 53 |
| flammability | Test Condition | Test Method | CELANESE USA/8211-55B100 |
|---|---|---|---|
| UL flame retardant rating | 1.1mm | UL 94 | HB |
| 2.9mm | UL 94 | HB |
| elastomer | Test Condition | Test Method | CELANESE USA/8211-55B100 |
|---|---|---|---|
| elongation | 断裂,23°C，横向 | ASTM D412 | 600 % |
| 断裂,23°C，横向 | ISO 37 | 600 % | |
| compression set | 125°C,70hr | ISO 815 | 55 % |
| 125°C,70hr | ASTM D395B | 55 % |
| aging | Test Condition | Test Method | CELANESE USA/8211-55B100 |
|---|---|---|---|
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | 4.0 |
| Change rate of tensile strength in air | 125°C,168hr | ISO 188 | -61 % |
| Shore hardness | ShoreA,23°C,168hr,inSodiumHydroxide,50% | ISO 1817 | 4.0 |
| Change rate of ultimate elongation in air | 23°C,168hr,inEthanol,95% | ASTM D471 | -3.0 % |
| Change rate of hardness (Shore) in the air | 邵氏A,125°C,168hr | ISO 188 | 8.0 |
| Change rate of tensile strength in air | 23°C,168hr,inHydrochloricAcid,10% | ISO 1817 | -1.0 % |
| 23°C,168hr,在水中 | ISO 1817 | 2.0 % | |
| Tensile stress change rate | 125°C,168hr，断裂 | ISO 188 | -70 % |
| 23°C,168hr,inEthanol,95%，断裂 | ISO 1817 | -3.0 % | |
| Change rate of tensile strength in air | 100°C,168hr | ASTM D573 | -28 % |
| 23°C,168hr,inSodiumHydroxide,50% | ISO 1817 | 1.0 % | |
| Change rate of ultimate elongation in air | 23°C,168hr,inIRM903Oil | ASTM D471 | -68 % |
| 23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | -7.0 % | |
| Change rate of tensile strength in air | 23°C,168hr,inIRM903Oil | ISO 1817 | -85 % |
| 100°C,168hr | ISO 188 | -28 % | |
| 23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | 1.0 % | |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inWater | ASTM D471 | 5.0 |
| Change rate of tensile strength in air | 23°C,168hr,inIRM903Oil | ASTM D471 | -85 % |
| 125°C,168hr | ASTM D573 | -61 % | |
| 23°C,168hr,inEthanol,95% | ASTM D471 | -17 % | |
| Change rate of hardness (Shore) in the air | ShoreA,100°C,168hr | ASTM D573 | -4.0 |
| Tensile stress change rate | 23°C,168hr,在水中，断裂 | ISO 1817 | -12 % |
| Change rate of hardness (Shore) in the air | ShoreA,100°C,168hr | ISO 188 | -4.0 |
| Change rate of tensile strength in air | 23°C,168hr,在水中 | ASTM D471 | 2.0 % |
| Shore hardness | ShoreA,23°C,168hr,inHydrochloricAcid,10% | ISO 1817 | 4.0 |
| Tensile stress change rate | 100°C,168hr，断裂 | ISO 188 | -14 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inIRM903Oil | ASTM D471 | -33 |
| Change rate of tensile strength in air | 23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | -1.0 % |
| Change rate of ultimate elongation in air | 23°C,168hr,在水中 | ASTM D471 | -12 % |
| 125°C,168hr | ASTM D573 | -70 % | |
| Tensile stress change rate | 23°C,168hr,inSodiumHydroxide,50%，断裂 | ISO 1817 | -7.0 % |
| Change rate of hardness (Shore) in the air | 邵氏A,125°C,168hr | ASTM D573 | 8.0 |
| Change rate of ultimate elongation in air | 100°C,168hr | ASTM D573 | -14 % |
| 23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | -9.0 % | |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | 4.0 |
| Shore hardness | ShoreA,23°C,168hr,inIRM903Oil | ISO 1817 | -33 |
| Tensile stress change rate | 23°C,168hr,inHydrochloricAcid,10%，断裂 | ISO 1817 | -9.0 % |
| Shore hardness | ShoreA,23°C,168hr,inEthanol,95% | ISO 1817 | 2.0 |
| ShoreA,23°C,168hr,inWater | ISO 1817 | 5.0 | |
| Tensile stress change rate | 23°C,168hr,inIRM903Oil，断裂 | ISO 1817 | -68 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inEthanol,95% | ASTM D471 | 2.0 |
| Change rate of tensile strength in air | 23°C,168hr,inEthanol,95% | ISO 1817 | -17 % |