物性数据
| 物理性能 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 熔体质量流动速率 | | ASTM D-1238 | 1 g/10min |
| 密度 | | ExxonMobil Method | 0.918 g/cm³ |
| 熔体质量流动速率 | 190°C/2.16kg | ASTMD1238 | 1.0 g/10min |
| 热性能 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 熔体温度 | | ExxonMobil Method | 119 °C |
| 光学性能 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 雾度 | | ASTM D-1003 | 18 % |
| 光泽度 | 纵向,45° | ASTM D-2457 | 42 |
| 光泽度 | 45° | ASTMD2457 | 39 |
| 雾度 | | ASTMD1003 | 18 % |
| 机械性能 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 屈服拉伸强度(MD) | @厚 150μ(5.9mil) | ASTM D-882 | 9 Mpa |
| 屈服拉伸强度(TD) | @厚 150μ(5.9mil) | ASTM D-882 | 9.7 Mpa |
| 断裂拉伸强度(MD) | @厚 150μ(5.9mil) | ASTM D-882 | 75.8 Mpa |
| 断裂拉伸强度(TD) | @厚 150μ(5.9mil) | ASTM D-882 | 62.7 Mpa |
| 断裂伸长率(MD) | @厚 150μ(5.9mil) | ASTM D-882 | 500 % |
| 断裂伸长率(TD) | @厚 150μ(5.9mil) | ASTM D-882 | 700 % |
| 1%正割模量(MD) | @厚 150μ(5.9mil) | ASTM D-882 | 183 Mpa |
| 1%正割模量(TD) | @厚 150μ(5.9mil) | ASTM D-882 | 205 Mpa |
| 落锤冲击强度 | F50 | ASTM D-1709A | 560 g |
| 埃尔门多夫撕裂强度 | MD | ASTM D-1922 | 280 g |
| 埃尔门多夫撕裂强度 | TD | ASTM D-1922 | 460 g |
| 穿刺能力 | | ExxonMobil Method | 4.3 J |
| 薄膜 | 测试条件 | 测试方法 | 测试结果 |
|---|
| 割线模量-1%Secant,MD | | ASTMD882 | 185 Mpa |
| 割线模量-1%Secant,TD | | ASTMD882 | 192 Mpa |
| 抗张强度 | 屈服 | ASTMD882 | 9.37 Mpa |
| 拉伸强度 | Yield | ASTMD882 | 9.40 Mpa |
| 抗张强度 | 断裂 | ASTMD882 | 54.3 Mpa |
| 抗张强度-TD | 断裂 | ASTMD882 | 42.7 Mpa |
| 伸长率 | 断裂 | ASTMD882 | 500 % |
| 拉伸应变 | Break | ASTMD882 | 600 % |
| 落锤冲击 | | ASTMD1709A | 460 g |
| 埃尔曼多夫抗撕强度-MD | | ASTMD1922 | 250 g |
| ElmendorfTearStrength-TD | | ASTMD1922 | 470 g |
| 其它性能 | 测试条件 | 测试方法 | 测试结果 |
|---|
| PPA | | | 有 |
| 抗粘连剂 | | | 否 |
| 滑爽剂 | | | 否 |
| 热稳定剂 | | | 有 |
免责声明：此数据表中的信息由 Plas.Com 从该材料的生产商或第三方处获得。Plas.Com 尽最大努力确保此数据的准确性。 但是 Plas.Com 对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。