MVLDPE 1018CA EXXONMOBIL USA
Exceed™
Shipping container、chip、film
High impact resistance、high strength
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | EXXONMOBIL USA/1018CA |
|---|---|---|---|
| Melt Temperature | ExxonMobil Method | 119 °C |
| Films Properties | Test Condition | Test Method | EXXONMOBIL USA/1018CA |
|---|---|---|---|
| Elongation - MD | 断裂 | ASTMD882 | 500 % |
| Elmendorf Tear Strength (MD) | ASTMD1922 | 250 g | |
| Gardner Impact | ASTMD1709A | 460 g | |
| Secant Modulus (1%Secant,TD) | ASTMD882 | 192 Mpa | |
| Tensile Strength (TD) | Yield | ASTMD882 | 9.40 Mpa |
| Elmendorf Tear Strength (TD) | ASTMD1922 | 470 g | |
| Tensile Strength-MD | 断裂 | ASTMD882 | 54.3 Mpa |
| Secant Modulus (1%Secant,MD) | ASTMD882 | 185 Mpa | |
| Tensile Strength-MD | 屈服 | ASTMD882 | 9.37 Mpa |
| Tensile Strain (TD) | Break | ASTMD882 | 600 % |
| Tensile Strength (TD) | 断裂 | ASTMD882 | 42.7 Mpa |
| Physical | Test Condition | Test Method | EXXONMOBIL USA/1018CA |
|---|---|---|---|
| Melt Mass-Flow Rate | 190°C/2.16kg | ASTMD1238 | 1.0 g/10min |
| ASTM D-1238 | 1 g/10min | ||
| Density | ExxonMobil Method | 0.918 g/cm³ |
| Mechanical Properties | Test Condition | Test Method | EXXONMOBIL USA/1018CA |
|---|---|---|---|
| Elmendorf Tear Strength | MD | ASTM D-1922 | 280 g |
| Tensile Strength (Yield) | @厚 150μ(5.9mil) | ASTM D-882 | 75.8 Mpa |
| Tensile Elongation (Break TD) | @厚 150μ(5.9mil) | ASTM D-882 | 700 % |
| Flexural Modulus - 1% Secant | @厚 150μ(5.9mil) | ASTM D-882 | 183 Mpa |
| Tensile Strength (Yield TD) | @厚 150μ(5.9mil) | ASTM D-882 | 9.7 Mpa |
| Tensile Strength (Break TD) | @厚 150μ(5.9mil) | ASTM D-882 | 62.7 Mpa |
| @厚 150μ(5.9mil) | ASTM D-882 | 205 Mpa | |
| Elmendorf Tear Strength | TD | ASTM D-1922 | 460 g |
| Tensile Strength (Yield MD) | @厚 150μ(5.9mil) | ASTM D-882 | 9 Mpa |
| Tensile Elongation (Break MD) | @厚 150μ(5.9mil) | ASTM D-882 | 500 % |
| Film Puncture Force | ExxonMobil Method | 4.3 J | |
| Instrumented Dart Impact | F50 | ASTM D-1709A | 560 g |
| Other | Test Condition | Test Method | EXXONMOBIL USA/1018CA |
|---|---|---|---|
| heat stabilizer | 有 | ||
| PPA | 有 | ||
| slip additive | 否 | ||
| anti-sticking agent | 否 |
| Optical | Test Condition | Test Method | EXXONMOBIL USA/1018CA |
|---|---|---|---|
| Haze | ASTM D-1003 | 18 % | |
| ASTMD1003 | 18 % | ||
| Gloss | 纵向,45° | ASTM D-2457 | 42 |
| 45° | ASTMD2457 | 39 |