ABS+PA POLYFLAM® RMMK 125
0
- 特性:可燃性
比对物性数据
| 测试条件 | 测试方法 | 测试结果 | |
|---|---|---|---|
| UL阻燃等级 | 1.5mm | UL 94 | V-0 |
| 3.0mm | UL 94 | V-0 | |
| 2.0mm | UL 94 | 5VA | |
| 1.5mm | IEC 60695-11-10,-20 | V-0 | |
| 3.0mm | IEC 60695-11-10,-20 | V-0 | |
| 2.0mm | IEC 60695-11-10,-20 | 5VA | |
| 灼热丝易燃指数 | 0.75mm | IEC 60695-2-12 | 960 °C |
| 1.5mm | IEC 60695-2-12 | 960 °C | |
| 密度 | ISO 1183/A | 1.30 g/cm³ | |
| 熔体体积流动速率 | 250°C/5.0kg | ISO 1133 | 12.0 cm³/10min |
| 拉伸模量 | ISO 527-2/1A/1 | 2500 MPa | |
| 燃烧速率 | 1.50mm,自动灭火 | ISO 3795 | 0.0 mm/min |
| 3.00mm,自动灭火 | ISO 3795 | 0.0 mm/min | |
| 热变形温度 | 0.45MPa,未退火，HDT | ISO 75-2/Bf | 113 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/Af | 60.0 °C | |
| 维卡软化温度 | -- | ISO 306/A50 | 190 °C |
| -- | ISO 306/B50 | 156 °C | |
| 球压硬度 | 125°C | IEC 60695-10-2 | Pass |
| RTI Elec | 1.5mm | UL 746 | 60.0 °C |
| 3.0mm | UL 746 | 60.0 °C | |
| RTI Imp | 1.5mm | UL 746 | 60.0 °C |
| 3.0mm | UL 746 | 60.0 °C | |
| RTI Str | 1.5mm | UL 746 | 60.060.0 °C |
| 相比耐漏电起痕指数 | IEC 60112 | PLC 3 | |
| 灼热丝易燃指数 | 3.0mm | IEC 60695-2-12 | 960 °C |
| 热灯丝点火温度 | 1.5mm | IEC 60695-2-13 | 750 °C |
| 3.0mm | IEC 60695-2-13 | 750 °C | |
| 极限氧指数 | ISO 4589-2 | 31 % | |
| 拉伸强度 | 屈服 | ISO 527-2/1A/50 | 52.0 MPa |
| 拉伸应变 | 屈服 | ISO 527-2/1A/50 | 3.0 % |
| 简支梁缺口冲击强度 | -30°C | ISO 179/1eA | 9.0 kJ/m² |
| 23°C | ISO 179/1eA | 12 kJ/m² | |
| 简支梁无缺口冲击强度 | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak |