ABS+PA POLYFLAM® RMMK 125 A SCHULMAN USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Test Condition | Test Method | A SCHULMAN USA/POLYFLAM® RMMK 125 | |
---|---|---|---|
Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 960 °C |
UL flame retardant rating | 3.0mm | UL 94 | V-0 |
RTI Elec | 3.0mm | UL 746 | 60.0 °C |
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 9.0 kJ/m² |
vicat | -- | ISO 306/B50 | 156 °C |
RTI Imp | 1.5mm | UL 746 | 60.0 °C |
RTI Str | 1.5mm | UL 746 | 60.060.0 °C |
Burning wire flammability index | 0.75mm | IEC 60695-2-12 | 960 °C |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
Tensile strain | 屈服 | ISO 527-2/1A/50 | 3.0 % |
UL flame retardant rating | 2.0mm | IEC 60695-11-10,-20 | 5VA |
1.5mm | IEC 60695-11-10,-20 | V-0 | |
RTI Imp | 3.0mm | UL 746 | 60.0 °C |
Tensile modulus | ISO 527-2/1A/1 | 2500 MPa | |
burning rate | 3.00mm,自动灭火 | ISO 3795 | 0.0 mm/min |
Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
tensile strength | 屈服 | ISO 527-2/1A/50 | 52.0 MPa |
UL flame retardant rating | 1.5mm | UL 94 | V-0 |
density | ISO 1183/A | 1.30 g/cm³ | |
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 12 kJ/m² |
UL flame retardant rating | 3.0mm | IEC 60695-11-10,-20 | V-0 |
burning rate | 1.50mm,自动灭火 | ISO 3795 | 0.0 mm/min |
RTI Elec | 1.5mm | UL 746 | 60.0 °C |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/Af | 60.0 °C |
0.45MPa,未退火,HDT | ISO 75-2/Bf | 113 °C | |
Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 750 °C |
1.5mm | IEC 60695-2-13 | 750 °C | |
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
vicat | -- | ISO 306/A50 | 190 °C |
Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 12.0 cm³/10min |
Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
UL flame retardant rating | 2.0mm | UL 94 | 5VA |
ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
Limiting Oxygen Index | ISO 4589-2 | 31 % |