- 特性:热性能
比对物性数据
| 测试条件 | 测试方法 | 测试结果 | |
|---|---|---|---|
| 脆化温度 | ASTM D746 | <-75.0 °C | |
| 变形 | UL 1581 | 1.0 % | |
| HotElongation-elongationunderload | 150°C | 内部方法 | 40 % |
| 绝缘电阻 | after12weeks:90°C | UL 1581 | 50000 Mohms/1000ft |
| 极限氧指数 | 4.00mm | ASTM D2863 | 24 % |
| 酸性气体释放 | HBr (溴化氢) | CSAC22.2No.0.3Method2 | 3.7 % |
| CrushingTest | UL 1581 | 635029 g | |
| 密度 | ASTM D792 | 1.01 g/cm³ | |
| 熔体质量流动速率 | 190°C/2.16kg | ASTM D1238 | 0.80 g/10min |
| 交联度 | ASTM D2765 | 67 % | |
| 拉伸强度 | 屈服 | UL 1581 | 12.4 MPa |
| 断裂 | UL 1581 | 13.8 MPa | |
| 断裂2 | UL 1581 | 13.4 MPa | |
| 断裂3 | UL 1581 | 12.8 MPa | |
| 断裂4 | UL 1581 | 12.6 MPa | |
| 伸长率 | 断裂 | UL 1581 | 380 % |
| 断裂2 | UL 1581 | 350 % | |
| 介电常数 | 1MHz | ASTM D150 | 2.34 |
| 100MHz | ASTM D150 | 2.34 | |
| 90°C,60Hz | UL 1581 | 2.50 | |
| 耗散因数 | 1MHz | ASTM D150 | 1.2E-03 |
| 100MHz | ASTM D150 | 8E-04 | |
| 介电强度 | -- | UL 1581 | 35000 V |
| afterglancingimpact | UL 1581 | 33000 V | |
| 绝缘电阻 | 23°C | UL 1581 | 560000 Mohms/1000ft |
| 90°C | UL 1581 | 21000 Mohms/1000ft | |
| 伸长率 | 断裂3 | UL 1581 | 330 % |
| WeatherometerAging | Elongationafterexposure | UL 1581 | 430 % |
| Originalelongation | UL 1581 | 440 % | |
| Originaltensilestrength | UL 1581 | 18.3 MPa | |
| Tensilestrengthafterexposure | UL 1581 | 19.8 MPa |