Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
XLPE Pexidan® X/T USA Saco Polymers
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Test Condition | Test Method | USA Saco Polymers/Pexidan® X/T | |
|---|---|---|---|
| Limiting Oxygen Index | 4.00mm | ASTM D2863 | 24 % |
| WeatherometerAging | Originaltensilestrength | UL 1581 | 18.3 MPa |
| CrushingTest | UL 1581 | 635029 g | |
| dielectric strength | -- | UL 1581 | 35000 V |
| deformation | UL 1581 | 1.0 % | |
| density | ASTM D792 | 1.01 g/cm³ | |
| Dissipation Factor | 1MHz | ASTM D150 | 1.2E-03 |
| insulation resistance | 90°C | UL 1581 | 21000 Mohms/1000ft |
| dielectric strength | afterglancingimpact | UL 1581 | 33000 V |
| elongation | 断裂 | UL 1581 | 380 % |
| dielectric constant | 90°C,60Hz | UL 1581 | 2.50 |
| WeatherometerAging | Tensilestrengthafterexposure | UL 1581 | 19.8 MPa |
| brittle temperature | ASTM D746 | <-75.0 °C | |
| dielectric constant | 100MHz | ASTM D150 | 2.34 |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.80 g/10min |
| elongation | 断裂2 | UL 1581 | 350 % |
| 断裂3 | UL 1581 | 330 % | |
| Degree of crosslinking | ASTM D2765 | 67 % | |
| WeatherometerAging | Elongationafterexposure | UL 1581 | 430 % |
| HotElongation | 150°C | 内部方法 | 40 % |
| WeatherometerAging | Originalelongation | UL 1581 | 440 % |
| dielectric constant | 1MHz | ASTM D150 | 2.34 |
| tensile strength | 屈服 | UL 1581 | 12.4 MPa |
| Dissipation Factor | 100MHz | ASTM D150 | 8E-04 |
| tensile strength | 断裂 | UL 1581 | 13.8 MPa |
| 断裂3 | UL 1581 | 12.8 MPa | |
| insulation resistance | after12weeks:90°C | UL 1581 | 50000 Mohms/1000ft |
| tensile strength | 断裂2 | UL 1581 | 13.4 MPa |
| insulation resistance | 23°C | UL 1581 | 560000 Mohms/1000ft |
| tensile strength | 断裂4 | UL 1581 | 12.6 MPa |
| AcidGasEmission-HBr | Test Condition | Test Method | USA Saco Polymers/Pexidan® X/T |
|---|---|---|---|
| Acid gas release | HBr (溴化氢) | CSAC22.2No.0.3Method2 | 3.7 % |