TPU IROGRAN® PS455-218 德国亨斯迈
25
比对物性数据
| 物理性能 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 熔体体积流动速率 | 177°C/2.16kg | 8.00 cm3/10min |
| 弹性体 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 拉伸强度 | 300%Strain,0.635mm | ASTM D412 | 4.83 Mpa |
| 300%Strain,0.635mm | DIN 53504 | 5.00 Mpa | |
| Break,0.635mm | ASTM D412 | 41.4 Mpa | |
| Break,0.635mm | DIN 53504 | 42.0 Mpa | |
| 压缩永久变形 | 23°C,70hr | DIN 53517 | 40 % |
| 70°C,24hr | DIN 53517 | 90 % | |
| 邵氏硬度 | ASTM D2632 | 50 % | |
| 拉伸应变 | Break,0.635mm | ASTM D412 | 700 % |
| Break,0.635mm | DIN 53504 | 700 % | |
| 撕裂强度 | 0.635mm | ASTM D624 | 66.5 kN/m |
| 0.635mm | DIN 53515 | 72 kN/m | |
| 压缩永久变形 | 23°C,70hr | ASTM D395 | 40 % |
| 70°C,24hr | ASTM D395 | 90 % | |
| 拉伸强度 | 100%Strain,0.635mm | ASTM D412 | 2.34 Mpa |
| 100%Strain,0.635mm | DIN 53504 | 2.00 Mpa |
| 硬度 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 邵氏硬度 | 邵氏A,注塑 | ASTM D2240 | 78 |
| ShoreA,InjectionMolded | DIN 53505 | 78 |
| 热性能 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| TMA | High:635.0µm | 内部方法 | 130 °C |
| Low:635.0µm | 内部方法 | 110 °C |
| 机械性能 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 耐磨性 | -- | ASTM D395 | 51 mm³ |
| -- | DIN 53516 | 50 mm³ |
免责声明：此数据表中的信息由 Plas.Com 从该材料的生产商或第三方处获得。Plas.Com 尽最大努力确保此数据的准确性。 但是 Plas.Com 对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。