PEEK 2400
0
- 特性:填料玻璃纤维增强材料
比对物性数据
| 物理性能 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 密度 | ASTMD792 | 1.53 g/cm³ |
| 硬度 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 肖氏硬度 | 邵氏D | ASTMD2240 | 90 |
| 机械性能 | 测试条件 | 测试方法 | 测试结果 |
|---|---|---|---|
| 拉伸模量 | ASTMD638 | 11600 MPa | |
| 抗张强度 | 屈服 | ASTMD638 | 198 MPa |
| 断裂 | ASTMD638 | 198 MPa | |
| 断裂,38°C | ASTMD638 | 193 MPa | |
| 断裂,93°C | ASTMD638 | 161 MPa | |
| 断裂,149°C | ASTMD638 | 117 MPa | |
| 断裂,204°C | ASTMD638 | 80.0 MPa | |
| 断裂,260°C | ASTMD638 | 66.2 MPa | |
| 断裂弯曲应变 | -- | ASTMD790 | 2.7 % |
| 38°C | ASTMD790 | 2.8 % | |
| 93°C | ASTMD790 | 2.6 % | |
| 抗张强度 | 断裂,316°C | ASTMD638 | 46.9 MPa |
| 伸长率 | 断裂 | ASTMD638 | 2.4 % |
| 弯曲模量 | -- | ASTMD790 | 11000 MPa |
| 38°C | ASTMD790 | 10700 MPa | |
| 93°C | ASTMD790 | 10600 MPa | |
| 149°C | ASTMD790 | 8650 MPa | |
| 204°C | ASTMD790 | 4540 MPa | |
| 260°C | ASTMD790 | 3250 MPa | |
| 316°C | ASTMD790 | 2090 MPa | |
| 弯曲强度 | 断裂 | ASTMD790 | 274 MPa |
| 压缩强度 | -- | ASTMD695 | 280 MPa |
| 38°C | ASTMD695 | 262 MPa | |
| 93°C | ASTMD695 | 210 MPa | |
| 149°C | ASTMD695 | 156 MPa | |
| 204°C | ASTMD695 | 87.6 MPa | |
| 260°C | ASTMD695 | 59.3 MPa | |
| 316°C | ASTMD695 | 31.0 MPa | |
| 剪切强度 | --3 | ASTMD732 | 121 MPa |
| --4 | ASTMD732 | 89.6 MPa | |
| 38°C3 | ASTMD732 | 112 MPa | |
| 38°C4 | ASTMD732 | 83.4 MPa | |
| 93°C3 | ASTMD732 | 90.3 MPa | |
| 93°C4 | ASTMD732 | 67.6 MPa | |
| 149°C4 | ASTMD732 | 53.1 MPa | |
| 204°C3 | ASTMD732 | 51.0 MPa | |
| 204°C4 | ASTMD732 | 33.8 MPa | |
| 弯曲强度 | 断裂,38°C | ASTMD790 | 274 MPa |
| 断裂,93°C | ASTMD790 | 241 MPa | |
| 断裂,149°C | ASTMD790 | 183 MPa | |
| 断裂,204°C | ASTMD790 | 121 MPa | |
| 断裂,260°C | ASTMD790 | 99.3 MPa | |
| 断裂,316°C | ASTMD790 | 69.6 MPa | |
| 剪切强度 | 149°C3 | ASTMD732 | 72.4 MPa |
| 260°C3 | ASTMD732 | 44.1 MPa | |
| 260°C4 | ASTMD732 | 29.0 MPa | |
| 316°C3 | ASTMD732 | 40.0 MPa | |
| 316°C4 | ASTMD732 | 24.1 MPa | |
| 断裂弯曲应变 | 149°C | ASTMD790 | 3.1 % |
| 204°C | ASTMD790 | 4.2 % | |
| 260°C | ASTMD790 | 4.7 % | |
| 316°C | ASTMD790 | 4.6 % |
免责声明：此数据表中的信息由 Plas.Com 从该材料的生产商或第三方处获得。Plas.Com 尽最大努力确保此数据的准确性。 但是 Plas.Com 对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。