Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEEK 2400 Arlon-MED
--
--
Fillers, glass fiber reinforced materials
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | Arlon-MED/ 2400 |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 90 |
| Mechanical properties | Test Condition | Test Method | Arlon-MED/ 2400 |
|---|---|---|---|
| shear strength | 316°C4 | ASTM D732 | 24.1 MPa |
| Flexural modulus | 38°C | ASTM D790 | 10700 MPa |
| -- | ASTM D790 | 11000 MPa | |
| shear strength | 316°C3 | ASTM D732 | 40.0 MPa |
| elongation | 断裂 | ASTM D638 | 2.4 % |
| Flexural modulus | 93°C | ASTM D790 | 10600 MPa |
| compressive strength | 316°C | ASTM D695 | 31.0 MPa |
| 204°C | ASTM D695 | 87.6 MPa | |
| Fracture bending strain | 204°C | ASTM D790 | 4.2 % |
| Flexural modulus | 260°C | ASTM D790 | 3250 MPa |
| Fracture bending strain | -- | ASTM D790 | 2.7 % |
| bending strength | 断裂,204°C | ASTM D790 | 121 MPa |
| Fracture bending strain | 38°C | ASTM D790 | 2.8 % |
| compressive strength | 149°C | ASTM D695 | 156 MPa |
| tensile strength | 断裂,38°C | ASTM D638 | 193 MPa |
| 断裂,149°C | ASTM D638 | 117 MPa | |
| shear strength | 149°C4 | ASTM D732 | 53.1 MPa |
| tensile strength | 屈服 | ASTM D638 | 198 MPa |
| shear strength | 38°C3 | ASTM D732 | 112 MPa |
| Fracture bending strain | 316°C | ASTM D790 | 4.6 % |
| shear strength | 38°C4 | ASTM D732 | 83.4 MPa |
| 149°C3 | ASTM D732 | 72.4 MPa | |
| 260°C4 | ASTM D732 | 29.0 MPa | |
| 260°C3 | ASTM D732 | 44.1 MPa | |
| Tensile modulus | ASTM D638 | 11600 MPa | |
| tensile strength | 断裂 | ASTM D638 | 198 MPa |
| bending strength | 断裂 | ASTM D790 | 274 MPa |
| tensile strength | 断裂,93°C | ASTM D638 | 161 MPa |
| 断裂,260°C | ASTM D638 | 66.2 MPa | |
| Flexural modulus | 316°C | ASTM D790 | 2090 MPa |
| shear strength | --3 | ASTM D732 | 121 MPa |
| --4 | ASTM D732 | 89.6 MPa | |
| bending strength | 断裂,93°C | ASTM D790 | 241 MPa |
| shear strength | 93°C4 | ASTM D732 | 67.6 MPa |
| bending strength | 断裂,316°C | ASTM D790 | 69.6 MPa |
| shear strength | 93°C3 | ASTM D732 | 90.3 MPa |
| bending strength | 断裂,38°C | ASTM D790 | 274 MPa |
| Fracture bending strain | 93°C | ASTM D790 | 2.6 % |
| compressive strength | 38°C | ASTM D695 | 262 MPa |
| Fracture bending strain | 260°C | ASTM D790 | 4.7 % |
| Flexural modulus | 149°C | ASTM D790 | 8650 MPa |
| compressive strength | 260°C | ASTM D695 | 59.3 MPa |
| Fracture bending strain | 149°C | ASTM D790 | 3.1 % |
| tensile strength | 断裂,316°C | ASTM D638 | 46.9 MPa |
| compressive strength | -- | ASTM D695 | 280 MPa |
| Flexural modulus | 204°C | ASTM D790 | 4540 MPa |
| compressive strength | 93°C | ASTM D695 | 210 MPa |
| bending strength | 断裂,149°C | ASTM D790 | 183 MPa |
| shear strength | 204°C3 | ASTM D732 | 51.0 MPa |
| 204°C4 | ASTM D732 | 33.8 MPa | |
| tensile strength | 断裂,204°C | ASTM D638 | 80.0 MPa |
| bending strength | 断裂,260°C | ASTM D790 | 99.3 MPa |
| physical property | Test Condition | Test Method | Arlon-MED/ 2400 |
|---|---|---|---|
| density | ASTM D792 | 1.53 g/cm³ |