Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.33到1.35 g/cm³ |
| melt mass-flow rate | | ISO1133 | 15 g/10min |
| Water absorption rate | | ISO62 | 5.3 % |
| Water absorption rate | | ISO62 | <0.15 % |
| Shrinkage rate | | 内部方法 | 0.80到1.0 % |
| Shrinkage rate | | 内部方法 | 0.45到0.55 % |
| Water absorption rate | | ISO62 | 0.50 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Burning wire flammability index | | IEC60695-2-12 | 750 °C |
| Limiting Oxygen Index | | ASTMD2863 | 27 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ReinforcementContent | | ISO3451 | 30 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO178 | 5400 MPa |
| Bending stress | | ISO178 | 160 MPa |
| Tensile modulus | | ISO527-2/1 | 5700 MPa |
| Tensile stress | Break | ISO527-2/50 | 100 MPa |
| Tensile strain | Break | ISO527-2/50 | 5.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 4.5 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 18 kJ/m² |
| Impact strength of cantilever beam gap | | ASTMD256 | 45 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC60093 | 7E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 21 kV/mm |
| dielectric constant | | IEC60250 | 3.80 |
| CTI | | IEC60112 | 500 V |
| CTI | | IEC60112 | 300 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| BallPressure Test | | IEC60695-10-2 | 通过 |
| melting temperature | | ISO11357-3 | 255 °C |
| | ISO75-2/A | 217 °C |
| Continuous use temperature | | IEC60216 | 90.0 °C |
| Continuous use temperature | | IEC60216 | 130 °C |
| vicat | | ISO306/A50 | 245 °C |
| vicat | | ISO306/B50 | 230 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.