Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 TAROMID A 280 G3 K3 Taro Plast S.p.A.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 G3 K3 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 4.5 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 45 J/m |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 18 kJ/m² |
| Supplementary Information | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 G3 K3 |
|---|---|---|---|
| ReinforcementContent | 750°C | ISO 3451 | 30 % |
| Mechanical properties | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 G3 K3 |
|---|---|---|---|
| Flexural modulus | ISO 178 | 5400 MPa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 5.0 % |
| Tensile modulus | ISO 527-2/1 | 5700 MPa | |
| bending strength | ISO 178 | 160 MPa | |
| tensile strength | 断裂 | ISO 527-2/50 | 100 MPa |
| Electrical performance | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 G3 K3 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 7E+15 ohms·cm | |
| dielectric constant | IEC 60250 | 3.80 | |
| dielectric strength | 2.00mm | IEC 60243-1 | 21 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 1 |
| 解决方案B | IEC 60112 | PLC 2 |
| flammability | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 G3 K3 |
|---|---|---|---|
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 750 °C |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| Limiting Oxygen Index | ASTM D2863 | 27 % |
| physical property | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 G3 K3 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.45to0.55 % |
| Water absorption rate | GranuleHumidity2 | ISO 62 | <0.15 % |
| 23°C,24hr | ISO 62 | 0.50 % | |
| 饱和,23°C | ISO 62 | 5.3 % | |
| Shrinkage rate | TD | 内部方法 | 0.80to1.0 % |
| density | ISO 1183 | 1.33to1.35 g/cm³ | |
| melt mass-flow rate | 280°C/2.16kg | ISO 1133 | 15 g/10min |
| Thermal performance | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 G3 K3 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 255 °C | |
| Continuous use temperature | --5 | IEC 60216 | 90.0 °C |
| vicat | -- | ISO 306/A50 | 245 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 217 °C |
| vicat | -- | ISO 306/B50 | 230 °C |
| Continuous use temperature | --6 | IEC 60216 | 130 °C |
| ball-indentation hardness | 205°C | IEC 60695-10-2 | 通过 |