Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.50 g/cm³ |
| Water absorption rate | | ASTM D570 | 0.11 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 118 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| limiting pv value | | | 12000 ft·lb/min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Wear factor | | ASTM D3702 | 40 10^-8mm³/N·m |
| coefficient of friction | Itself - Static | | 0.070 |
| Tensile modulus | | ASTM D638 | 2340 MPa |
| tensile strength | | ASTM D638 | 48.3 MPa |
| elongation | | ASTM D638 | 10 % |
| Flexural modulus | | ASTM D790 | 2410 MPa |
| bending strength | | ASTM D790 | 86.2 MPa |
| coefficient of friction | | | 0.12 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 53 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 168 °C |
| Heat distortion temperature | | ASTM D648 | 118 °C |
| Heat distortion temperature | Melting Temperature | ASTM D648 | 175 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 9.2E-05 cm/cm/°C |
| Long term maximum operating temperature | | | 85 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.