POM Homopolymer TECAFORM® HPV13 ENSINGER GERMANY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ENSINGER GERMANY/TECAFORM® HPV13 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 53 J/m |
| Supplementary Information | Test Condition | Test Method | ENSINGER GERMANY/TECAFORM® HPV13 |
|---|---|---|---|
| limiting pv value | 12000 ft·lb/min |
| hardness | Test Condition | Test Method | ENSINGER GERMANY/TECAFORM® HPV13 |
|---|---|---|---|
| Rockwell hardness | R级,23°C | ASTM D785 | 118 |
| Mechanical properties | Test Condition | Test Method | ENSINGER GERMANY/TECAFORM® HPV13 |
|---|---|---|---|
| coefficient of friction | 与自身-动态2 | 0.12 | |
| tensile strength | 断裂,23°C | ASTM D638 | 48.3 MPa |
| bending strength | 23°C | ASTM D790 | 86.2 MPa |
| coefficient of friction | 与自身-静态 | 0.070 | |
| Tensile modulus | 23°C | ASTM D638 | 2340 MPa |
| Flexural modulus | 23°C | ASTM D790 | 2410 MPa |
| Wear factor | 0.28MPa,0.25m/sec | ASTM D3702 | 40 10^-8mm³/N·m |
| elongation | 断裂,23°C | ASTM D638 | 10 % |
| physical property | Test Condition | Test Method | ENSINGER GERMANY/TECAFORM® HPV13 |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.11 % |
| density | ASTM D792 | 1.50 g/cm³ |
| Thermal performance | Test Condition | Test Method | ENSINGER GERMANY/TECAFORM® HPV13 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 118 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 168 °C | |
| 熔融温度，HDT | ASTM D648 | 175 °C | |
| Long term maximum operating temperature | 85 °C | ||
| Linear coefficient of thermal expansion | MD | ASTM D696 | 9.2E-05 cm/cm/°C |