HDPE SF 5008E
0
- Usages:Filmbag
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D1505 | 0.950 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 0.050 g/10min | |
| ASTM D1238 | 15 g/10min | ||
| Environmental stress cracking resistance | ASTM D1693 | >500 hr |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact Strength | ASTM D3420 | 34.3 J/cm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flexural modulus | ASTM D790 | 1100 MPa |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation | ASTM D882 | 500 % | |
| ASTM D882 | 700 % | ||
| Dart impact | ASTM D1709 | 130 g | |
| Elmendorf tear strength | ASTM D1922 | 6.9 kN/m | |
| ASTM D1922 | 147.1 kN/m | ||
| film thickness | 20 µm | ||
| Tensile modulus | ASTM D882 | 850 MPa | |
| ASTM D882 | 1050 MPa | ||
| tensile strength | ASTM D882 | 100 MPa | |
| ASTM D882 | 55.0 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| brittle temperature | ASTM D746 | <-70.0 °C | |
| melting temperature | ASTM D3418 | 132 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.