Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
HDPE SF 5008E Chandra Asri Petrochemical
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Chandra Asri Petrochemical/SF 5008E |
|---|---|---|---|
| Impact Strength | 20.0µm，吹膜 | ASTM D3420 | 34.3 J/cm |
| film | Test Condition | Test Method | Chandra Asri Petrochemical/SF 5008E |
|---|---|---|---|
| Elmendorf tear strength | TD:20.0µm | ASTM D1922 | 147.1 kN/m |
| Tensile modulus | 20µm,吹塑薄膜，TD | ASTM D882 | 1050 MPa |
| Dart impact | 20µm,吹塑薄膜 | ASTM D1709 | 130 g |
| Tensile modulus | 20µm,吹塑薄膜，MD | ASTM D882 | 850 MPa |
| film thickness | 20 µm | ||
| Elmendorf tear strength | MD:20.0µm | ASTM D1922 | 6.9 kN/m |
| tensile strength | TD:断裂,20µm,吹塑薄膜 | ASTM D882 | 55.0 MPa |
| elongation | MD:断裂,20µm,吹塑薄膜 | ASTM D882 | 500 % |
| TD:断裂,20µm,吹塑薄膜 | ASTM D882 | 700 % | |
| tensile strength | MD:断裂,20µm,吹塑薄膜 | ASTM D882 | 100 MPa |
| Mechanical properties | Test Condition | Test Method | Chandra Asri Petrochemical/SF 5008E |
|---|---|---|---|
| Flexural modulus | ASTM D790 | 1100 MPa |
| physical property | Test Condition | Test Method | Chandra Asri Petrochemical/SF 5008E |
|---|---|---|---|
| density | ASTM D1505 | 0.950 g/cm³ | |
| melt mass-flow rate | 190°C/21.6kg | ASTM D1238 | 15 g/10min |
| Environmental stress cracking resistance | F50 | ASTM D1693 | >500 hr |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.050 g/10min |
| Thermal performance | Test Condition | Test Method | Chandra Asri Petrochemical/SF 5008E |
|---|---|---|---|
| brittle temperature | ASTM D746 | <-70.0 °C | |
| melting temperature | ASTM D3418 | 132 °C |