POM Homopolymer LNP™ LUBRICOMP™ KP004AH compound
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ASTM D570 | 0.20 % | |
| density | ASTM D792 | 1.49 g/cm³ | |
| ISO 1183 | 1.49 g/cm³ | ||
| Shrinkage rate | ASTM D955 | 2.1 % | |
| ASTM D955 | 2.1 % | ||
| ISO 294-4 | 2.1 % | ||
| ISO 294-4 | 2.1 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2210 MPa | |
| bending strength | ASTM D790 | 75.8 MPa | |
| ISO 178 | 77.0 MPa | ||
| coefficient of friction | ASTM D3702Modified | 0.25 | |
| ASTM D3702Modified | 0.16 | ||
| Wear factor | ASTM D3702Modified | 9.00 10^-10in^5-min/ft-lb-hr | |
| Tensile modulus | ISO 527-2/1 | 2600 MPa | |
| tensile strength | Break | ASTM D638 | 50.3 MPa |
| Break | ISO 527-2 | 45.0 MPa | |
| elongation | Break | ASTM D638 | 13 % |
| Tensile strain | Break | ISO 527-2 | 11 % |
| Flexural modulus | ASTM D790 | 2410 MPa | |
| ISO 178 | 2800 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D4812 | 430 J/m | |
| Suspended wall beam without notch impact strength | ISO 180/1U | 30 kJ/m² | |
| Dart impact | ASTM D3763 | 5.00 J | |
| Impact strength of cantilever beam gap | ASTM D256 | 48 J/m | |
| ISO 180/1A | 4.5 kJ/m² | ||
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 1.00 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 163 °C | |
| ASTM D648 | 99.4 °C | ||
| ISO 75-2/Af | 99.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.