POM Homopolymer LNP™ LUBRICOMP™ KP004AH compound SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC/LNP™ LUBRICOMP™ KP004AH compound
Suspended wall beam without notch impact strength23°CISO 180/1U30 kJ/m²
Impact strength of cantilever beam gap23°CASTM D25648 J/m
Multi axis Instrumented Impact EnergyISO 6603-21.00 J
Impact strength of cantilever beam gap23°CASTM D4812430 J/m
23°CISO 180/1A4.5 kJ/m²
Dart impact23°C,EnergyatPeakLoadASTM D37635.00 J
Mechanical propertiesTest ConditionTest MethodSABIC/LNP™ LUBRICOMP™ KP004AH compound
tensile strength 断裂ISO 527-245.0 MPa
Wear factorWasherASTM D3702Modified9.00 10^-10in^5-min/ft-lb-hr
bending strengthASTM D79075.8 MPa
Flexural modulusISO 1782800 MPa
bending strengthISO 17877.0 MPa
elongation断裂ASTM D63813 %
coefficient of frictionStaticASTM D3702Modified0.16
Tensile modulusASTM D6382210 MPa
tensile strength 断裂ASTM D63850.3 MPa
Tensile strain断裂ISO 527-211 %
Flexural modulusASTM D7902410 MPa
coefficient of frictionDynamicASTM D3702Modified0.25
Tensile modulusISO 527-2/12600 MPa
physical property Test ConditionTest MethodSABIC/LNP™ LUBRICOMP™ KP004AH compound
Shrinkage rateMD:24小时ISO 294-42.1 %
MD：24小时ASTM D9552.1 %
Water absorption rate24hr,50%RHASTM D5700.20 %
densityASTM D7921.49 g/cm³
ISO 11831.49 g/cm³
Shrinkage rateTD：24hrASTM D9552.1 %
TD:24小时ISO 294-42.1 %
Thermal performanceTest ConditionTest MethodSABIC/LNP™ LUBRICOMP™ KP004AH compound
Heat distortion temperature0.45MPa,未退火,3.20mm，HDTASTM D648163 °C
1.8MPa,未退火,64.0mm跨距，HDTISO 75-2/Af99.0 °C
1.8MPa,未退火,3.20mm，HDTASTM D64899.4 °C