Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| | | 按重量计算的混合比:100,按容量计算的混合比:100 |
| | | 按重量计算的混合比:42,按容量计算的混合比:50 |
| Thermosetting mixed viscosity | | ASTMD4878 | 550 cP |
| stripping time | | | 1400 min |
| GelTime | | ASTMD2971 | 1.0 hr |
| physical property | Test Condition | Test Method | Test Result |
|---|
| Weight Percubicinch | | | 18 g |
| density | | ASTMD4669 | 1.07 g/cm³ |
| Shrinkage rate | | ASTMD2566 | 0.050到0.25 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ASTMD2240 | 80 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 2530 MPa |
| tensile strength | | ASTMD638 | 55.8 MPa |
| elongation | Break | ASTMD638 | 15 % |
| Flexural modulus | | ASTMD790 | 2700 MPa |
| bending strength | | ASTMD790 | 66.9 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 29 J/m |
| Suspended wall beam without notch impact strength | | ASTMD256 | 46 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | 7.3E+13 ohms·cm |
| dielectric strength | | ASTMD149 | 21 kV/mm |
| dielectric constant | | ASTMD150 | 4.10 |
| dielectric constant | | ASTMD150 | 3.80 |
| Dissipation Factor | | ASTMD150 | 0.012 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Service | | | 63 °C |
| thermal conductivity | | | 0.22 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.