| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | % | 0.90 -- |
| Shrinkage rate | | % | 0.20 -- |
| Water absorption rate | | % | 3.0 -- |
| Water absorption rate | | % | 0.30 -- |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | V-0 -- |
| Burning wire flammability index | | °C | 960 -- |
| Burning wire flammability index | | °C | 960 -- |
| Hot filament ignition temperature | | °C | 800 -- |
| Hot filament ignition temperature | | °C | 875 -- |
| UL flame retardant rating | | | V-0 -- |
| UL flame retardant rating | | | V-0 -- |
| UL flame retardant rating | | | V-0 -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | | 12000 MPa |
| tensile strength | | MPa | 150 145 |
| Tensile strain | | % | 2.2 2.5 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | kJ/m² | 42 -- |
| Impact strength of simply supported beam without notch | | kJ/m² | 45 48 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ohms | 1E+11 -- |
| Volume resistivity | | ohms·cm | 1E+12 -- |
| dielectric strength | | kV/mm | 35 -- |
| Compared to the Leakage Tracking Index (CTI) | | V | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | °C | 280 -- |
| Continuous use temperature | | °C | 140 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.