PC LUVOCOM® 50-1396 LEHVOSS Group

Properties:
Fillers
glass
carbon fiber reinforced materials
Usages:
Engineering accessories
gears
medical
nursing supplies
business equipment
sports equipment
Compare

Technical Data Sheet

physical property	Test Method	Test Result
density	ISO 1183	1.36 g/cm³
melt mass-flow rate	ISO 1133	27 g/10min
Melt volume flow rate	ISO 1133	22.0 cm³/10min
Shrinkage rate	DIN 16901	0.10to0.40 %
Water absorption rate		<0.20 %

Mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Break	ISO 527-2	120 MPa
Tensile strain	Yield	ISO 527-2	2.0 %
Bending Strain		ISO 178	2.5 %
Flexural modulus		ISO 178	8500 MPa
bending strength		ISO 178	185 MPa
coefficient of friction			0.25
coefficient of friction	coefficient of friction			0.20
Tensile modulus		ISO 527-2	10000 MPa

Impact resistance	Test Method	Test Result
Charpy Notched Impact Strength	ISO 179/1eA	9.0 kJ/m²
Impact strength of simply supported beam without notch	ISO 179/1fU	25 kJ/m²
Charpy Notched Impact Strength	ISO 179/1eA	12 kJ/m²
Impact strength of simply supported beam without notch	ISO 179/1fU	22 kJ/m²

Electrical performance	Test Condition	Test Method	Test Result
Surface Resistivity		IEC 60093	<1.0E+2 ohms

Thermal performance	Test Method	Test Result
maximum service temperature		150 °C
vicat	ISO 306/A	160 °C
Linear coefficient of thermal expansion	DIN 53752	2.5E-05 cm/cm/°C
thermal conductivity	DIN 52612	0.45 W/m/K
Continuous use temperature	UL 746B	130 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.