Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC LUVOCOM® 50-1396 LEHVOSS Group
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LEHVOSS Group/LUVOCOM® 50-1396 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1fU | 22 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 12 kJ/m² |
| -30°C | ISO 179/1eA | 9.0 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1fU | 25 kJ/m² |
| Mechanical properties | Test Condition | Test Method | LEHVOSS Group/LUVOCOM® 50-1396 |
|---|---|---|---|
| tensile strength | 断裂 | ISO 527-2 | 120 MPa |
| coefficient of friction | Static | 0.20 | |
| Tensile modulus | ISO 527-2 | 10000 MPa | |
| Tensile strain | 屈服 | ISO 527-2 | 2.0 % |
| Bending Strain | ISO 178 | 2.5 % | |
| Flexural modulus | ISO 178 | 8500 MPa | |
| bending strength | ISO 178 | 185 MPa | |
| coefficient of friction | Dynamic | 0.25 |
| Electrical performance | Test Condition | Test Method | LEHVOSS Group/LUVOCOM® 50-1396 |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | <1.0E+2 ohms |
| physical property | Test Condition | Test Method | LEHVOSS Group/LUVOCOM® 50-1396 |
|---|---|---|---|
| Melt volume flow rate | 300°C/5.0kg | ISO 1133 | 22.0 cm³/10min |
| Shrinkage rate | DIN 16901 | 0.10to0.40 % | |
| melt mass-flow rate | 300°C/5.0kg | ISO 1133 | 27 g/10min |
| Water absorption rate | 23°C,24hr | <0.20 % | |
| density | ISO 1183 | 1.36 g/cm³ |
| Thermal performance | Test Condition | Test Method | LEHVOSS Group/LUVOCOM® 50-1396 |
|---|---|---|---|
| thermal conductivity | DIN 52612 | 0.45 W/m/K | |
| Continuous use temperature | UL 746B | 130 °C | |
| vicat | ISO 306/A | 160 °C | |
| Linear coefficient of thermal expansion | MD | DIN 53752 | 2.5E-05 cm/cm/°C |
| maximum service temperature | ShortTerm | 150 °C |