GPPS TAIRIREX® GP550N（白底）
527
- Properties:currencyhigh molecular weight
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 2.3 g/10 min |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB | |
| Residual Monomer | < 700 ppm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 3040 Mpa | |
| tensile strength | ASTM D638 | 51.0 Mpa | |
| elongation | ASTM D638 | 2.0 % | |
| Flexural modulus | ASTM D790 | 3330 Mpa | |
| bending strength | ASTM D790 | 98.0 Mpa |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 75 °C | ||
| drying time | 1.0 to 2.0 hr | ||
| Hopper temperature | 40 °C | ||
| Temperature at the rear of the barrel | 195 °C | ||
| Temperature in the middle of the barrel | 210 to 220 °C | ||
| Temperature at the front of the material cylinder | 215 °C | ||
| Processing (melt) temperature | 190 to 230 °C | ||
| Temperature | 20 to 70 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 95.0 °C | |
| vicat | ASTM D1525 | 104 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.