Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
GPPS GP550N（白底） FCFC TAIWAN
TAIRIREX®
--
currency、high molecular weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | FCFC TAIWAN/GP550N（白底） |
|---|---|---|---|
| Vicat Softening Temperature | ASTM D1525, ISO 306 | 104 °C | |
| Deflection Temperature Under Load? | 1.8 MPa, 退火, 3.18 mm | ASTM D648, ISO 75-2/A | 95.0 °C |
| Injection | Test Condition | Test Method | FCFC TAIWAN/GP550N（白底） |
|---|---|---|---|
| Middle Temperature | 210 到 220 °C | ||
| Processing (Melt) Temp | 190 到 230 °C | ||
| Drying Time | 1.0 到 2.0 hr | ||
| Rear Temperature | 195 °C | ||
| Drying Temperature | 75 °C | ||
| Front Temperature | 215 °C | ||
| Hopper Temperature | 40 °C | ||
| Mold Temperature | 20 到 70 °C |
| Physical | Test Condition | Test Method | FCFC TAIWAN/GP550N（白底） |
|---|---|---|---|
| Melt Mass-Flow Rate | 200°C/5.0 kg | ASTM D1238, ISO 1133 | 2.3 g/10 min |
| Mechanical Properties | Test Condition | Test Method | FCFC TAIWAN/GP550N（白底） |
|---|---|---|---|
| Flexural Strength | 23°C | ASTM D790, ISO 178 | 98.0 Mpa |
| Tensile Modulus | 23°C | ASTM D638, ISO 527-2 | 3040 Mpa |
| Tensile Strength | 23°C | ASTM D638, ISO 527-2 | 51.0 Mpa |
| Flexural Modulus | 23°C | ASTM D790, ISO 178 | 3330 Mpa |
| Tensile Elongation | 断裂, 23°C | ASTM D638, ISO 527-2 | 2.0 % |
| Flammability | Test Condition | Test Method | FCFC TAIWAN/GP550N（白底） |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm, NC | UL 94 | HB |
| Residual monomer | < 700 ppm |