Technical Data Sheet
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | | 90% |
| Fuzzy coefficient (Haze) | | ISO 14782 | 83% % |
| transmittance | | ASTM D1003/ISO 13468 | 90 % |
| refractive index | | ASTM D542/ISO 489 | 1.632 |
| processability | Test Condition | Test Method | Test Result |
|---|
| Dry conditions | | | 80°-90°五小时以上 |
| process temperature | | | 300 ℃（℉） |
| process temperature | | | 250 ℃（℉） |
| process temperature | | | 280 ℃（℉） |
| process temperature | | | 230 ℃（℉） |
| screw speed | | | 20mm/s rpm |
| Temperature | | | 100-120 ℃（℉） |
| Melt Temperature | | | 280 ℃（℉） |
| other | Test Condition | Test Method | Test Result |
|---|
| notes | | | 800万像素镜头 |
| | | 耐热，折射率优良 |
| colour | | | 透明 |
| purpose | | | 800万像素镜头，光学镜片 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Charpy impact strength | | ASTM D256/ISO 179 | 43 kg·cm/cm(J/M)ft·lb/in |
| Izod notch impact strength | | ASTM D256/ISO 179 | 45 kg·cm/cm(J/M)ft·lb/in |
| Tensile elongation at break (elongation at break) | | ASTM D638/ISO 527 | 2500 kg/cm²(MPa)[Lb/in²] |
| elongation | | ASTM D638/ISO 527 | 2500 % |
| Flexural modulus | | ASTM D790/ISO 178 | 65 kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 115 kg/cm²(MPa)[Lb/in²] |
| tensile strength | | ASTM D638/ISO 527 | 65 kg/cm²(MPa)[Lb/in²] |
| Tensile modulus | | ASTM D638/ISO 527 | 10 kg/cm²(MPa)[Lb/in²] |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 1.26 |
| Mold Shrinkage | | ASTM D955 | 0.7 % |
| melt mass-flow rate | | ASTM D1238/ISO 1133 | 3 g/10min |
| melt mass-flow rate | | ASTM D1238/ISO 1133 | 10 g/10min |
| Water absorption rate | | ASTM D570/ISO 62 | 0.2 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| glass transition temperature | | ASTM D785 | 142 ℃（℉） |
| | ASTM D648/ISO 75 | 128 ℃（℉） |
| Combustibility (rate) | | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.