PEEK LUVOCOM® 1105-9020/T LEHVOSS Group
0
- Properties:Fillerscarbon fiber reinforced materials
- Usages:Applications in the automotive industrybushingsmedicalnursing suppliestextile applicationspumpsaerospace applicationsengineering accessoriesgearsbearings
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.62 g/cm³ | |
| Shrinkage rate | ISO 294-4 | 0.2 % | |
| ISO 294-4 | 0.6 % | ||
| Water absorption rate | ISO 62 | <=0.1 % | |
| melt mass-flow rate | ISO 1133 | 15 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ISO 527-2 | 155 MPa | |
| elongation at break | ISO 527-2 | 1.6 % | |
| bending strength | ISO 178 | 215 MPa | |
| Flexural modulus | ISO 178 | 13000 MPa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 28 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | 30 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor | <=1.0E+5 Ω.cm | ||
| <=1.0E+7 Ω.cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | 250 °C | ||
| 270 °C | |||
| vicat | ISO 306/A50 | 320 °C | |
| Heat distortion temperature | ISO 75-2/Af | 260 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.