PEEK LUVOCOM® 1105-9020/T LEHVOSS Group
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | LEHVOSS Group/LUVOCOM® 1105-9020/T |
|---|---|---|---|
| Dissipation Factor | 表面电阻 | <=1.0E+7 Ω.cm | |
| 体积电阻 | <=1.0E+5 Ω.cm |
| Mechanical properties | Test Condition | Test Method | LEHVOSS Group/LUVOCOM® 1105-9020/T |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 13000 MPa |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 28 kJ/m² |
| bending strength | 应变2.1％，23°C | ISO 178 | 215 MPa |
| tensile strength | 23°C | ISO 527-2 | 155 MPa |
| elongation at break | 23°C | ISO 527-2 | 1.6 % |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 30 kJ/m² |
| physical property | Test Condition | Test Method | LEHVOSS Group/LUVOCOM® 1105-9020/T |
|---|---|---|---|
| Water absorption rate | (23°C,24hr) | ISO 62 | <=0.1 % |
| Shrinkage rate | TD | ISO 294-4 | 0.6 % |
| melt mass-flow rate | 380℃/10.0Kg | ISO 1133 | 15 g/10min |
| Shrinkage rate | MD | ISO 294-4 | 0.2 % |
| density | ISO 1183 | 1.62 g/cm³ |
| Thermal performance | Test Condition | Test Method | LEHVOSS Group/LUVOCOM® 1105-9020/T |
|---|---|---|---|
| vicat | ISO 306/A50 | 320 °C | |
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 260 °C |
| Linear coefficient of thermal expansion | 最高使用温度 | 270 °C |