Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.00 -- |
| Shrinkage rate | | % | 1.3 -- |
| Shrinkage rate | | % | 0.80 -- |
| Water absorption rate | | % | 1.5 -- |
| Water absorption rate | | % | 0.70 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | MPa | 55.0 -- |
| Shore hardness | | | 68 -- |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | | HB -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 900 -- |
| tensile strength | Yield | MPa | 35.0 -- |
| tensile strength | Break | MPa | 40.0 40.0 |
| Tensile strain | Yield | % | 12 -- |
| Tensile strain | Break | % | >50 -- |
| Nominal tensile fracture strain | | % | >50 -- |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 13 -- |
| Charpy Notched Impact Strength | | kJ/m² | 55 -- |
| Impact strength of simply supported beam without notch | | | 无断裂 |
| Impact strength of simply supported beam without notch | | | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ohms | -- 1E+12 |
| Volume resistivity | | ohms·cm | -- 1E+13 |
| dielectric strength | | kV/mm | 22 -- |
| Compared to the Leakage Tracking Index (CTI) | | V | -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | °C | 85.0 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 1.2E-04 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 1.4E-04 -- |
| Heat distortion temperature | | °C | 40.0 -- |
| Continuous use temperature | | °C | 90.0to110 -- |
| Continuous use temperature | | °C | 140 -- |
| melting temperature | | °C | 179 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.