Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus		ASTM D790	6760	MPa
bending strength		ASTM D790	49.3	MPa
Compressive modulus		ASTM D695	3450	MPa
compressive strength		ASTM D695	62.1	MPa
Tensile modulus		ASTM D638	1700	MPa
tensile strength		ASTM D638	40.3	MPa
elongation	Break	ASTM D638	4.0	%
Bending modulus		ASTM D790	1700	MPa
bending strength		ASTM D790	57.1	MPa
compressive strength		ASTM D695	60.4	MPa
Tensile modulus		ASTM D638	3000	MPa
tensile strength		ASTM D638	21.4	MPa
elongation	Break	ASTM D638	0.40	%
Compressive modulus		ASTM D695	534	MPa
thermosetting	Test Condition	Test Method	Test Result	Test Unit
storage stability	23°C	ASTM D2471	3.0	min
storage stability	storage stability	23°C	ASTM D2471	2.5	min
Thermosetting mixed viscosity		ASTM D2393	100	cP
Post curing time	121°C		4.0to6.0	hr
Thermosetting components	PartA		按重量计算的混合比:120.按容量计算的混合比:100
Thermosetting components	Thermosetting components	PartB		按重量计算的混合比:100.按容量计算的混合比:100
Thermosetting mixed viscosity		ASTM D2393	3000	cP
stripping time	23°C		60	min
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	57.2	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	121	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD	ASTM D2566	0.060	%
density		ASTM D1475	1.09	g/cm³
Specific volume		ASTM D1475	1.00	cm³/g
Shrinkage rate	MD	ASTM D2566	1.0	%
density		ASTM D1475	1.60	g/cm³
Specific volume		ASTM D1475	0.625	cm³/g
hardness	Test Condition	Test Method	Test Result	Test Unit
Shore hardness	ShoreD	ASTM D2240	85
Shore hardness	Shore hardness	ShoreD	ASTM D2240	80
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
CureTime	23°C		10.0to15.0	min
Mixing Ratio			1A:4Bbyvolume1A:5Bbyweight

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.