| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D955 | 0.50 % |
| Water absorption rate | Saturation | ASTM D570 | 0.60 % |
| density | | ASTM D792 | 1.61 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.20 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 775 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 15000 MPa |
| tensile strength | Yield | ASTM D638 | 180 MPa |
| elongation | Break | ASTM D638 | 2.0 % |
| Flexural modulus | | ASTM D790 | 15000 MPa |
| bending strength | | ASTM D790 | 285 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180/A | 8.0 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180 | 45 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648A | 250 °C |
| vicat | | ASTM D15253 | 250 °C |
| RTI Elec | | UL 746 | 140 °C |
| RTI Imp | | UL 746 | 140 °C |
| RTI | | UL 746 | 140 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.