PA66 VAMPAMID 66 5030 V0 P VAMP TECH ITALY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | VAMP TECH ITALY/VAMPAMID 66 5030 V0 P |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180/A | 8.0 kJ/m² | |
| Suspended wall beam without notch impact strength | ISO 180 | 45 kJ/m² |
| Mechanical properties | Test Condition | Test Method | VAMP TECH ITALY/VAMPAMID 66 5030 V0 P |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 2.0 % |
| Tensile modulus | ASTM D638 | 15000 MPa | |
| Flexural modulus | ASTM D790 | 15000 MPa | |
| tensile strength | 屈服 | ASTM D638 | 180 MPa |
| bending strength | ASTM D790 | 285 MPa |
| Electrical performance | Test Condition | Test Method | VAMP TECH ITALY/VAMPAMID 66 5030 V0 P |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 |
| flammability | Test Condition | Test Method | VAMP TECH ITALY/VAMPAMID 66 5030 V0 P |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | V-0 |
| Hot filament ignition temperature | 1.0到2.0mm | IEC 60695-2-13 | 775 °C |
| Burning wire flammability index | 1.0到2.0mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 0.8mm | UL 94 | V-0 |
| 1.6mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | VAMP TECH ITALY/VAMPAMID 66 5030 V0 P |
|---|---|---|---|
| Water absorption rate | 饱和 | ASTM D570 | 0.60 % |
| Shrinkage rate | MD | ASTM D955 | 0.20 % |
| TD | ASTM D955 | 0.50 % | |
| density | ASTM D792 | 1.61 g/cm³ |
| Thermal performance | Test Condition | Test Method | VAMP TECH ITALY/VAMPAMID 66 5030 V0 P |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648A | 250 °C |
| vicat | ASTM D15253 | 250 °C | |
| RTI Imp | UL 746 | 140 °C | |
| RTI | UL 746 | 140 °C | |
| RTI Elec | UL 746 | 140 °C |