Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D955 | 0.50to0.70 % |
| Water absorption rate | Equilibrium | ASTM D570 | 0.10 % |
| density | | ASTM D792 | 1.23 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 15 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 114 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2600 MPa |
| tensile strength | | ASTM D638 | 59.0 MPa |
| elongation | Break | ASTM D638 | 5.0 % |
| Flexural modulus | | ASTM D790 | 2700 MPa |
| bending strength | | ASTM D790 | 91.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 450 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | 30 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Volume resistivity | | ASTM D257 | 1E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 93.0 °C |
| vicat | | ASTM D15252 | 120 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare