Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS Triapol® Blends C3 K55 CNZ0062 BS301 Brazil Petropol
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Brazil Petropol/Triapol® Blends C3 K55 CNZ0062 BS301 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 450 J/m |
| hardness | Test Condition | Test Method | Brazil Petropol/Triapol® Blends C3 K55 CNZ0062 BS301 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 114 |
| Mechanical properties | Test Condition | Test Method | Brazil Petropol/Triapol® Blends C3 K55 CNZ0062 BS301 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 5.0 % |
| tensile strength | ASTM D638 | 59.0 MPa | |
| Tensile modulus | ASTM D638 | 2600 MPa | |
| Flexural modulus | ASTM D790 | 2700 MPa | |
| bending strength | ASTM D790 | 91.0 MPa |
| Electrical performance | Test Condition | Test Method | Brazil Petropol/Triapol® Blends C3 K55 CNZ0062 BS301 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
| Volume resistivity | ASTM D257 | 1E+15 ohms·cm | |
| dielectric strength | ASTM D149 | 30 kV/mm |
| flammability | Test Condition | Test Method | Brazil Petropol/Triapol® Blends C3 K55 CNZ0062 BS301 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | Brazil Petropol/Triapol® Blends C3 K55 CNZ0062 BS301 |
|---|---|---|---|
| melt mass-flow rate | 230°C/5.0kg | ASTM D1238 | 15 g/10min |
| Shrinkage rate | MD | ASTM D955 | 0.50to0.70 % |
| Water absorption rate | 平衡 | ASTM D570 | 0.10 % |
| density | ASTM D792 | 1.23 g/cm³ |
| Thermal performance | Test Condition | Test Method | Brazil Petropol/Triapol® Blends C3 K55 CNZ0062 BS301 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 93.0 °C |
| vicat | ASTM D15252 | 120 °C |