Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.16 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 3.00 cm³/10min |
| Shrinkage rate | | ISO 294-4 | 0.20to0.40 % |
| ash content | | | 16 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039-1 | 135 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 6.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 20 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 18 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/A | 5.0 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/A | 7.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179 | 5.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-2 | 74.0 MPa |
| tensile strength | | ISO 527-2 | 74.0 MPa |
| Tensile strain | | ISO 527-2 | 2.0 % |
| Flexural modulus | | ISO 178 | 5400 MPa |
| bending strength | | ISO 178 | 101 MPa |
| Tensile modulus | | ISO 527-2 | 5500 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+14 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 32 kV/mm |
| relative permittivity | | IEC 60250 | 2.90 |
| relative permittivity | | IEC 60250 | 3.10 |
| Dissipation Factor | | IEC 60250 | 5E-03 |
| Dissipation Factor | | IEC 60250 | 6E-03 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 106 °C |
| Heat distortion temperature | | ISO 75-2/A | 102 °C |
| vicat | | ISO 306/B50 | 105 °C |
| Linear coefficient of thermal expansion | | ISO 11359-1 | 4E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.