Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | | 0.35to0.55 % |
| density | | ISO 1183 | 1.24to1.30 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 3.0to18 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 65to70 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Hot filament ignition temperature | | VDE0471/2 | 960 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 4000to7500 MPa |
| tensile strength | Yield | ISO 527-2 | 50.0to80.0 MPa |
| Tensile strain | Break | ISO 527-2 | >4.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180/1A | >8.0 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ISO 3146 | 160 °C |
| Heat distortion temperature | | ISO 75-2/A | 110 °C |
| vicat | | ISO 306/B | 110 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare