PA66

PA66 Zytel® 80G33L DUPONT CANADA

Properties:
Thermal stability
Usages:
Automotive interior partsElectrical applications
Certificates:
UL
Compare View Prices

Technical Data Sheet

Filling analysis	Test Method	Test Result
Thermal Conductivity of Melt		0.22 W/m/K
Emission of Organic Compounds	VDA 277	25.0 µgC/g
Odor	VDA 270	3.00
Specific Heat Capacity of Melt		2200 J/kg/°C
Top out temperature		210 °C
Melt density		1.12 g/cm³

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	74 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	80 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	91 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	80 kJ/m²

flammability	Test Condition	Test Method	Test Result
FMVSS combustion rate		FMVSS 302	SE/B
Extreme Oxygen Index		ISO 4589-2	23 %
UL flame retardant rating		UL 94	HB
UL flame retardant rating	UL flame retardant rating		UL 94	HB
雾化 - G-value (condensate)		ISO 6452	8.0E-4 g
Burning rate	1.00 mm	ISO 3795	23 mm/min

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus		ISO 178	7400 Mpa
Tensile strain	Break	ISO 527-2	4.0 %
tensile strength	Break	ISO 527-2	142 Mpa
Tensile modulus		ISO 527-2	8700 Mpa

injection	Test Condition	Test Result
Maintain pressure	Drying Recommended	yes
Hold Pressure Time		3.00 s/mm
Maximum Screw Tangential Speed		12 m/min
drying temperature		80 °C
Drying time - hot air dryer		2.0 to 4.0 hr
Suggested maximum moisture content		0.20 %
Processing (melt) temperature		285 to 305 °C
Melt Temperature, Optimum		295 °C
Mold temperature		50 to 100 °C
Mold Temperature, Optimum		80 °C
Maintain pressure		50.0 to 100 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	1.2E-4 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.5E-5 cm/cm/°C
Melting temperature		ISO 11357-3	262 °C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	247 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	262 °C
Effective thermal diffusivity coefficient			8.50E-8 m²/s

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	横向Flow	ISO 294-4	0.80 %
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	0.30 %
Water absorption rate	24 hr, 23°C	ISO 62	0.83 %
	Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	4.5 %
	Water absorption rate	Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	1.5 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index		IEC 60112	V

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.