Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 80G33L DUPONT CANADA
Zytel®
Automotive interior parts、Electrical applications
Thermal stability
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT CANADA/80G33L |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 80 kJ/m² |
| 23°C | ISO 180/1U | 74 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 91 kJ/m² |
| -30°C | ISO 179/1eU | 80 kJ/m² |
| Mechanical properties | Test Condition | Test Method | DUPONT CANADA/80G33L |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 8700 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 4.0 % |
| Flexural modulus | ISO 178 | 7400 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 142 Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT CANADA/80G33L |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| flammability | Test Condition | Test Method | DUPONT CANADA/80G33L |
|---|---|---|---|
| 雾化 - G-value (condensate) | ISO 6452 | 8.0E-4 g | |
| UL flame retardant rating | UL 94 | HB | |
| Limiting Oxygen Index | ISO 4589-2 | 23 % | |
| FMVSS combustion rate | FMVSS 302 | SE/B | |
| burning rate | 1.00 mm | ISO 3795 | 23 mm/min |
| Filling analysis | Test Condition | Test Method | DUPONT CANADA/80G33L |
|---|---|---|---|
| Ejection Temperature | 210 °C | ||
| Odor | VDA 270 | 3.00 | |
| Thermal Conductivity of Melt | 0.22 W/m/K | ||
| Melt density | 1.12 g/cm³ | ||
| Emission of Organic Compounds | VDA 277 | 25.0 µgC/g | |
| Specific Heat Capacity of Melt | 2200 J/kg/°C |
| physical property | Test Condition | Test Method | DUPONT CANADA/80G33L |
|---|---|---|---|
| Water absorption rate | 饱和, 23°C, 2.00 mm | ISO 62 | 4.5 % |
| 平衡, 23°C, 2.00 mm, 50% RH | ISO 62 | 1.5 % | |
| 24 hr, 23°C | ISO 62 | 0.83 % | |
| Shrinkage rate | 流量 | ISO 294-4 | 0.30 % |
| 横向流量 | ISO 294-4 | 0.80 % |
| Thermal performance | Test Condition | Test Method | DUPONT CANADA/80G33L |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 262 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 262 °C |
| Effective thermal diffusivity coefficient | 8.50E-8 m²/s | ||
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 247 °C |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 1.5E-5 cm/cm/°C |
| 横向 | ISO 11359-2 | 1.2E-4 cm/cm/°C |
| injection | Test Condition | Test Method | DUPONT CANADA/80G33L |
|---|---|---|---|
| pressure holding | 50.0 to 100 Mpa | ||
| Maximum Screw Tangential Speed | 12 m/min | ||
| pressure holding | Drying Recommended | yes | |
| Suggested maximum moisture content | 0.20 % | ||
| Drying time - hot air dryer | 2.0 to 4.0 hr | ||
| Processing (melt) temperature | 285 to 305 °C | ||
| drying temperature | 80 °C | ||
| Temperature | 50 to 100 °C | ||
| Melt Temperature, Optimum | 295 °C | ||
| Hold Pressure Time | 3.00 s/mm | ||
| Mold Temperature, Optimum | 80 °C |